{"title":"Ultra-fine ferrite grains obtained in the TSDR process","authors":"Ling Zhang , Wangyue Yang , Chunxia Xue , Zuqing Sun","doi":"10.1016/S1005-8850(08)60106-1","DOIUrl":null,"url":null,"abstract":"<div><p>By careful design of rolling schedule, ultra-fine (∼2 μm) ferrite grains in a low carbon high niobium (0.09wt%Nb) micro-alloying steel with average austenite grain sizes above 800 μm can be achieved in the simulated thin slab direct rolling process. The 5-pass deformation was divided into two stages: the refinement of austenite through complete recrystallization and the refinement of ferrite through dynamic strain-induced transformation. The effects of Nb in solution and strain-induced NbCN precipitates on the ferrite transformation were also extensively discussed.</p></div>","PeriodicalId":100851,"journal":{"name":"Journal of University of Science and Technology Beijing, Mineral, Metallurgy, Material","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2008-10-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1016/S1005-8850(08)60106-1","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of University of Science and Technology Beijing, Mineral, Metallurgy, Material","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S1005885008601061","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
By careful design of rolling schedule, ultra-fine (∼2 μm) ferrite grains in a low carbon high niobium (0.09wt%Nb) micro-alloying steel with average austenite grain sizes above 800 μm can be achieved in the simulated thin slab direct rolling process. The 5-pass deformation was divided into two stages: the refinement of austenite through complete recrystallization and the refinement of ferrite through dynamic strain-induced transformation. The effects of Nb in solution and strain-induced NbCN precipitates on the ferrite transformation were also extensively discussed.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们