Jae-Chan Jo, Kwang-Sam Kim, In-Taek Im, Dae-hwan Kim, Sung-Yong Shim, Su-gun Lim
{"title":"Effects of Mg Addition on Heat Treatment and Mechanical Properties of A356 Alloy","authors":"Jae-Chan Jo, Kwang-Sam Kim, In-Taek Im, Dae-hwan Kim, Sung-Yong Shim, Su-gun Lim","doi":"10.7777/JKFS.2016.36.6.195","DOIUrl":null,"url":null,"abstract":"The effects of Mg addition on heat treatment and mechanical properties of A356 alloy were investigated. With increased amounts of Mg addition to A356 alloy, the grain size decreased and eutectic Si was refined. And, this process can improve the mechanical properties. Solid solution heat treatment causes the spheroidizing of eutectic Si. In this study, although eutectic Si was refined with Mg addition, solid solution time increased from 2 hours to 6 hours with Mg addition, and aging time also increased, from 4 hours to 8 hours. After heat treatment, Mg2Si remained in a formation of Chinese script. And, Chinese script Mg2Si formed with Mg addition caused a reduction of the elongation of the alloys according to the stress concentration.","PeriodicalId":16318,"journal":{"name":"Journal of Korea Foundry Society","volume":"13 1","pages":"195-201"},"PeriodicalIF":0.0000,"publicationDate":"2016-12-09","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Korea Foundry Society","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.7777/JKFS.2016.36.6.195","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
The effects of Mg addition on heat treatment and mechanical properties of A356 alloy were investigated. With increased amounts of Mg addition to A356 alloy, the grain size decreased and eutectic Si was refined. And, this process can improve the mechanical properties. Solid solution heat treatment causes the spheroidizing of eutectic Si. In this study, although eutectic Si was refined with Mg addition, solid solution time increased from 2 hours to 6 hours with Mg addition, and aging time also increased, from 4 hours to 8 hours. After heat treatment, Mg2Si remained in a formation of Chinese script. And, Chinese script Mg2Si formed with Mg addition caused a reduction of the elongation of the alloys according to the stress concentration.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们