J. I. Carreno-Saavedra, T. Ros-Yáñez, C. I. Garcia, E. Hernández-Durán, R. A. Iquilio, F. M. Castro Cerda
{"title":"Application of ultrafast heating and tempering to plate steel","authors":"J. I. Carreno-Saavedra, T. Ros-Yáñez, C. I. Garcia, E. Hernández-Durán, R. A. Iquilio, F. M. Castro Cerda","doi":"10.1080/02670836.2023.2202020","DOIUrl":null,"url":null,"abstract":"The microstructure and tensile properties were studied in a low-alloy steel plate treated under ultra-fast heating, quenching, and tempering. The microstructure after heat-treatments was predominantly martensite, with low fraction of bainite and ferrite. The tensile tests showed a 100 MPa improvement in strength and a doubling of the total elongation with the increase in heating rate. The tempering process considerably enhanced the ductility from 1–4% to up to 14% in the samples treated at fast heating rates..Furthermore, the work hardening capacity of ultra-fast heated steel was superior compared to steel treated under conventional quenching and tempering. The results suggest that the tempering stage after ultra-fast heat-treatments and quenching further improves the properties compared to the standard quenched and tempered condition.","PeriodicalId":18232,"journal":{"name":"Materials Science and Technology","volume":"1 1","pages":"2417 - 2432"},"PeriodicalIF":2.2000,"publicationDate":"2023-04-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Science and Technology","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/02670836.2023.2202020","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0
Abstract
The microstructure and tensile properties were studied in a low-alloy steel plate treated under ultra-fast heating, quenching, and tempering. The microstructure after heat-treatments was predominantly martensite, with low fraction of bainite and ferrite. The tensile tests showed a 100 MPa improvement in strength and a doubling of the total elongation with the increase in heating rate. The tempering process considerably enhanced the ductility from 1–4% to up to 14% in the samples treated at fast heating rates..Furthermore, the work hardening capacity of ultra-fast heated steel was superior compared to steel treated under conventional quenching and tempering. The results suggest that the tempering stage after ultra-fast heat-treatments and quenching further improves the properties compared to the standard quenched and tempered condition.
期刊介绍：
《Materials Science and Technology》（MST） is an international forum for the publication of refereed contributions covering fundamental and technological aspects of materials science and engineering.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们