{"title":"PREPARATION AND SWELLING PROPERTIES OF POLY(3,4 –ETHYLENEDIOXYTHIOPHENE)/POLY(ACRYLIC ACID)/BENTONITE COMPOSITE HYDROGELS","authors":"K. Hüner","doi":"10.30931/jetas.1001134","DOIUrl":null,"url":null,"abstract":"In this study, poly(acrylic acid) (PAA)/bentonite (BNT) composites were synthesized through chemical crosslinking by a chemical polymerization using ammonium persulfate as initiator and N,N’-methylenebisacrylamide as crosslinker. Poly(3,4-ethylenedioxythiophene) (PEDOT) was synthesized by oxidative polymerization and then PEDOT/PAA/BNT composites were prepared by mixing PEDOT at 5%, 10% and 20% by mass into PAA/BNT composite. These hydrogel composites were characterized by FTIR, XRD and SEM. It was observed that water absorbency increased with the increase of PEDOT ratio of hydrogel composites.","PeriodicalId":7757,"journal":{"name":"Anadolu University Journal of Science and Technology-A Applied Sciences and Engineering","volume":"23 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2022-10-22","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Anadolu University Journal of Science and Technology-A Applied Sciences and Engineering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.30931/jetas.1001134","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
In this study, poly(acrylic acid) (PAA)/bentonite (BNT) composites were synthesized through chemical crosslinking by a chemical polymerization using ammonium persulfate as initiator and N,N’-methylenebisacrylamide as crosslinker. Poly(3,4-ethylenedioxythiophene) (PEDOT) was synthesized by oxidative polymerization and then PEDOT/PAA/BNT composites were prepared by mixing PEDOT at 5%, 10% and 20% by mass into PAA/BNT composite. These hydrogel composites were characterized by FTIR, XRD and SEM. It was observed that water absorbency increased with the increase of PEDOT ratio of hydrogel composites.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们