K. E. Chekurov, A. Barabanova, I. V. Blagodatskhikh, A. Peregudov, A. Khokhlov
{"title":"Synthesis and Repellent Properties of Fluorinated Diblock-Copolymers","authors":"K. E. Chekurov, A. Barabanova, I. V. Blagodatskhikh, A. Peregudov, A. Khokhlov","doi":"10.17677/FN20714807.2019.02.01","DOIUrl":null,"url":null,"abstract":"The radical polymerization of 2,3,4,5,6-pentafluorostyrene (PFS) and 2-hydroxyethyl methacrylate (HEMA) in the presence of chain transfer agent 4-cyano-4(phenylcarbonothioylthio)pentanoic acid was studied. It was shown that PFS polymerization proceeds through a reversible addition-fragmentation chain transfer polymerization mechanism, and that of HEMA polymerization is more complicated. The conditions of preparation of diblock copolymers (DBC) which do not contained the by-products of uncontrolled radical polymerization of PFS were found. Comparative study of contact angles versus water (θ2 ) and diiodomethane (θ2 I 2) of nylon fabric samples, treated with DBC containing 37 mol. % PFSunits, and poly-2,3,4,5,6-pentafluorostyrene (PPFS) was conducted. It is shown that the nylon fabric treated with DBC has higher θ2 О = 125 3o and θ2 I 2 = 1015o than PPFS films (θ Н 2 О = 102 2o иθ2 I 2 = 741o).","PeriodicalId":12217,"journal":{"name":"Fluorine Notes","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2019-04-14","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"2","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Fluorine Notes","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.17677/FN20714807.2019.02.01","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 2
Abstract
The radical polymerization of 2,3,4,5,6-pentafluorostyrene (PFS) and 2-hydroxyethyl methacrylate (HEMA) in the presence of chain transfer agent 4-cyano-4(phenylcarbonothioylthio)pentanoic acid was studied. It was shown that PFS polymerization proceeds through a reversible addition-fragmentation chain transfer polymerization mechanism, and that of HEMA polymerization is more complicated. The conditions of preparation of diblock copolymers (DBC) which do not contained the by-products of uncontrolled radical polymerization of PFS were found. Comparative study of contact angles versus water (θ2 ) and diiodomethane (θ2 I 2) of nylon fabric samples, treated with DBC containing 37 mol. % PFSunits, and poly-2,3,4,5,6-pentafluorostyrene (PPFS) was conducted. It is shown that the nylon fabric treated with DBC has higher θ2 О = 125 3o and θ2 I 2 = 1015o than PPFS films (θ Н 2 О = 102 2o иθ2 I 2 = 741o).
研究了2,3,4,5,6-五氟苯乙烯(PFS)和2-甲基丙烯酸羟乙酯(HEMA)在链转移剂4-氰基-4(苯基羰基硫代)戊酸存在下的自由基聚合反应。结果表明，PFS聚合是通过可逆加成-破碎链转移聚合机理进行的，而HEMA聚合的机理更为复杂。找到了制备不含PFS自由基聚合副产物的双嵌段共聚物(DBC)的条件。用含有37 mol. % PFSunits的DBC和聚2,3,4,5,6-五氟苯乙烯(PPFS)处理尼龙织物样品，比较了其与水(θ2)和二碘甲烷(θ2 I 2)的接触角。结果表明，DBC处理后的尼龙织物的θ2 О = 12530和θ2 I 2 = 10150比PPFS膜(θ Н 2 О = 10220 иθ2 I 2 = 7410)高。
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们