S. Husain, N. H. Haryanti, S. Suryajaya, Antung Permitaria
{"title":"SYNTHESIS AND CHARACTERIZATION OF CALCIUM SILICATE FROM RICE HUSK ASH AND SNAIL SHELL","authors":"S. Husain, N. H. Haryanti, S. Suryajaya, Antung Permitaria","doi":"10.18860/neu.v11i2.6608","DOIUrl":null,"url":null,"abstract":"<p class=\"abstrak\">Calcium silicate ceramics have been made using natural ingredients such as rice husk and snail shell with solid reaction techniques. The aim of this study to determine the characteristics of calcium silicate that have been sintered at a temperature of 900 <sup>°</sup>C, 1000 <sup>°</sup>C, and 1100 <sup>°</sup>C. Samples were characterized by X-Ray Diffraction (XRD), optical microscopy, and Fourier Transform Infra-Red (FTIR). The results of XRD characterization showed that CaSiO<sub>3</sub> (calcium silicate) along with the increase in calcination temperature and quantity was increased due to the increase of temperature of calcination. FTIR analysis showed that the Ca-Si-O bond was formed at wave number ranging from 848 cm<sup>-1</sup> and 999 – 1001 cm<sup>-1</sup>.</p>","PeriodicalId":17685,"journal":{"name":"Jurnal Neutrino","volume":"35 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2019-09-17","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"6","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Jurnal Neutrino","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.18860/neu.v11i2.6608","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 6
Abstract
Calcium silicate ceramics have been made using natural ingredients such as rice husk and snail shell with solid reaction techniques. The aim of this study to determine the characteristics of calcium silicate that have been sintered at a temperature of 900 °C, 1000 °C, and 1100 °C. Samples were characterized by X-Ray Diffraction (XRD), optical microscopy, and Fourier Transform Infra-Red (FTIR). The results of XRD characterization showed that CaSiO3 (calcium silicate) along with the increase in calcination temperature and quantity was increased due to the increase of temperature of calcination. FTIR analysis showed that the Ca-Si-O bond was formed at wave number ranging from 848 cm-1 and 999 – 1001 cm-1.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们