{"title":"10 -2 s -1 压缩应变率下Al-Teflon的反应现象","authors":"冯彬, 方向, 李裕春, 王怀玺, 毛益明","doi":"10.11943/J.ISSN.1006-9941.2016.06.015","DOIUrl":null,"url":null,"abstract":"采用不同的热处理工艺, 得到了A类(烧结温度380 ℃, 降温速率50 ℃·h-1)、B类(烧结温度350 ℃, 降温速率70 ℃·h-1)两类Al-Teflon反应材料。通过准静态压缩实验对两类试件反应现象进行了测试。得到了应力应变曲线。进行了试件密度测量, SEM微观形貌分析及高速摄影观察。结果表明, B类试件发生剧烈放热反应, A类试件没有反应发生。B类试件的应变硬化模量是A类试件的5.3倍, 其在应力应变平面的反应区间为:真实应变1.2~2.2, 真实应力60~80 MPa。A、B两类试件结晶度分别为63%和43%。在A类试件中发现大量纳米级聚四氟乙烯纤丝, 可能对材料裂纹拓展起阻碍作用。B类试件的反应现象与试件的强剪切作用及脆性开裂现象密切相关。","PeriodicalId":35753,"journal":{"name":"Hanneng Cailiao/Chinese Journal of Energetic Materials","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2016-06-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Hanneng Cailiao/Chinese Journal of Energetic Materials","FirstCategoryId":"1087","ListUrlMain":"https://doi.org/10.11943/J.ISSN.1006-9941.2016.06.015","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"Engineering","Score":null,"Total":0}
引用次数: 0
引用
批量引用
10 -2 s -1 压缩应变率下Al-Teflon的反应现象
采用不同的热处理工艺, 得到了A类(烧结温度380 ℃, 降温速率50 ℃·h-1)、B类(烧结温度350 ℃, 降温速率70 ℃·h-1)两类Al-Teflon反应材料。通过准静态压缩实验对两类试件反应现象进行了测试。得到了应力应变曲线。进行了试件密度测量, SEM微观形貌分析及高速摄影观察。结果表明, B类试件发生剧烈放热反应, A类试件没有反应发生。B类试件的应变硬化模量是A类试件的5.3倍, 其在应力应变平面的反应区间为:真实应变1.2~2.2, 真实应力60~80 MPa。A、B两类试件结晶度分别为63%和43%。在A类试件中发现大量纳米级聚四氟乙烯纤丝, 可能对材料裂纹拓展起阻碍作用。B类试件的反应现象与试件的强剪切作用及脆性开裂现象密切相关。
本文章由计算机程序翻译,如有差异,请以英文原文为准。