Xulong An, Xiaotong Zhang, Y. Sui, Jing Hu, Zhengxiang Xu, Wei Wei, C. Chu, Wenwen Sun
{"title":"Microstructure and solidification behaviour of CuNiSiAl eutectic multi-principal element alloy","authors":"Xulong An, Xiaotong Zhang, Y. Sui, Jing Hu, Zhengxiang Xu, Wei Wei, C. Chu, Wenwen Sun","doi":"10.1080/02670836.2023.2210917","DOIUrl":null,"url":null,"abstract":"Eutectic multi-principal element alloys show great promise due to their exceptional castability, unique near-equilibrium microstructure, and controllability. In this study, a novel copper-containing Cu42.3Ni30Si15Al12.7 eutectic multi-principal element alloy was designed and investigated. The microstructure of the alloy is composed of primary phase Ni2Si and eutectic phase (FCC(Cu) + BCC(NiAl)). The eutectic reaction temperature is 1004°C. Understanding the solidification process is crucial for optimising solidification parameters and subsequent annealing. The as-cast Cu42.3Ni30Si15Al12.7 alloy exhibits high micro-hardness (400 ± 2.4 HV) and compressive fracture strength (1511 MPa)","PeriodicalId":18232,"journal":{"name":"Materials Science and Technology","volume":"297 1","pages":"2556 - 2561"},"PeriodicalIF":1.7000,"publicationDate":"2023-05-14","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Science and Technology","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/02670836.2023.2210917","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 1
Abstract
Eutectic multi-principal element alloys show great promise due to their exceptional castability, unique near-equilibrium microstructure, and controllability. In this study, a novel copper-containing Cu42.3Ni30Si15Al12.7 eutectic multi-principal element alloy was designed and investigated. The microstructure of the alloy is composed of primary phase Ni2Si and eutectic phase (FCC(Cu) + BCC(NiAl)). The eutectic reaction temperature is 1004°C. Understanding the solidification process is crucial for optimising solidification parameters and subsequent annealing. The as-cast Cu42.3Ni30Si15Al12.7 alloy exhibits high micro-hardness (400 ± 2.4 HV) and compressive fracture strength (1511 MPa)
期刊介绍：
《Materials Science and Technology》（MST） is an international forum for the publication of refereed contributions covering fundamental and technological aspects of materials science and engineering.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们