{"title":"Cellulose Acetate-Graft-Poly (Methyl Methacrylate): A andldquo;Graft fromandrdquo; Approach of Nitroxide Mediated Radical Polymerization","authors":"V. Mbah, A. Celli, R. Cipolletti, S. Sabbatini, P. Stipa","doi":"10.35248/2157-7048.20.11.399","DOIUrl":null,"url":null,"abstract":"Poly (methyl methacrylate) was grafted onto cellulose acetate backbone using a “graft from” of Nitroxide Mediated Radical Polymerization (NMRP). The formation of cellulose acetate-co-poly (methyl methacrylate) using N-tert-butyl- N- (1-diethylphosphono-2,2-dimethylpropyl) (SG1)-nitroxide based macroalkoxyamine system was confirmed by FTIR and NMR analyses. The copolymer exhibited living characteristics as shown by NMR. DSC investigations showed a copolymer with a rich poly (methyl methacrylate) phase around 120°C and a rich cellulose acetate phase at around 175°C.","PeriodicalId":15308,"journal":{"name":"Journal of Chemical Engineering & Process Technology","volume":"1 1","pages":"1-6"},"PeriodicalIF":0.0000,"publicationDate":"2020-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Chemical Engineering & Process Technology","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.35248/2157-7048.20.11.399","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
Poly (methyl methacrylate) was grafted onto cellulose acetate backbone using a “graft from” of Nitroxide Mediated Radical Polymerization (NMRP). The formation of cellulose acetate-co-poly (methyl methacrylate) using N-tert-butyl- N- (1-diethylphosphono-2,2-dimethylpropyl) (SG1)-nitroxide based macroalkoxyamine system was confirmed by FTIR and NMR analyses. The copolymer exhibited living characteristics as shown by NMR. DSC investigations showed a copolymer with a rich poly (methyl methacrylate) phase around 120°C and a rich cellulose acetate phase at around 175°C.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们