Y. Gorbatkina, O. Zhuravleva, V. G. Ivanova-Mumzhieva, V. Chebotarev
{"title":"The Influence of the Molecular Weight of Polysulphone on the Adhesion of Epoxy/Polysulphone Binders to Fibres:","authors":"Y. Gorbatkina, O. Zhuravleva, V. G. Ivanova-Mumzhieva, V. Chebotarev","doi":"10.1177/0307174X1804500503","DOIUrl":null,"url":null,"abstract":"The concentration dependences of the adhesive strength, τ, of joints of 150 μm diameter steel wire and modified epoxy binder were investigated. The modifier used was PSK-1 polysulphone of different molecular weight, M. The concentration, C, of PSK-1 was varied from 5 to 20 wt%. It was shown that the form of the τ-C curves changes with change in M. At M = 5000 and 10 000, τ is not dependent on C; at M = 17 000 and 27 000, the τ-C relationship is described by a curve with a maximum. At M = 35 000 and 42 000, the adhesive strength decreases with increase in C. The factors affecting the measured value of τ in the case of epoxides modified with heat-resistant thermoplastics are considered.","PeriodicalId":14443,"journal":{"name":"International polymer science and technology","volume":"11 1","pages":"201-204"},"PeriodicalIF":0.0000,"publicationDate":"2018-09-04","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"2","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"International polymer science and technology","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1177/0307174X1804500503","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 2
Abstract
The concentration dependences of the adhesive strength, τ, of joints of 150 μm diameter steel wire and modified epoxy binder were investigated. The modifier used was PSK-1 polysulphone of different molecular weight, M. The concentration, C, of PSK-1 was varied from 5 to 20 wt%. It was shown that the form of the τ-C curves changes with change in M. At M = 5000 and 10 000, τ is not dependent on C; at M = 17 000 and 27 000, the τ-C relationship is described by a curve with a maximum. At M = 35 000 and 42 000, the adhesive strength decreases with increase in C. The factors affecting the measured value of τ in the case of epoxides modified with heat-resistant thermoplastics are considered.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们