The Effect of Colloidal Silica and Glaze Coatings on the Adhesion of Zirconia with Various Ytrria Concentration.

Abstract

Purpose: This study evaluated the effect of coating traditional and translucent Y-TZP with an industrial nanometric colloidal silica or glaze before or after sintering on the adhesion of zirconia with various ytrria concentration.

Materials and methods: Specimens of Y-TZP with 3% and 5% yttria were subdivided into 5 groups (n=10), according to the coating applied and moment of application (before or after Y-TZP sintering): Control (no coating), Colloidal Silica/Sintering, Sintering/Colloidal Silica, Glaze/Sintering, Sintering/ Glaze. Lithium disilicate (LD) was used as positive control. Except for Y-TZP controls, groups were conditioned with silane before cementation with a self-adhesive resin cement. After 24 hours, the shear bond strength and failure analysis were performed. Also, analysis of specimens' surface was accomplished with SEM-EDX. Kruskal-Wallis and Dunn tests were applied to analyze differences between groups (p⟨0.05).

Results: Overall, the worst and best values of shear bond strength test were control and glaze after sintering groups. Different morphological and chemical aspects were observed in SEM-EDX analysis.

Conclusions: Coating Y-TZP with colloidal silica showed unsatisfactory results. In 3Y-TZP, the surface treatment associated with the best adhesion values was the application of glaze after zirconia sintering. However, in 5Y-TZP, glaze application can be performed before or after the zirconia sintering to optimize clinical steps.