Effect of Nystatin with and without DMAHDM on Antifungal and Mechanical Properties of Acrylic Resins.

Abstract

Purpose: To investigate antifungal and mechanical properties after the impregnation of Dimethyl Amino-ethyl Hexa-decyl Di-methacrylate (DMAHDM) alone or in combination with Nystatin in polymethylmethacrylate.

Methodology: The control group was fabricated by mixing powder and liquid of PMMA at the ratio of 2.5:1 g/mL. The DMAHDM was added to PMMA liquid and were mixed with PMMA powder. The Nystatin (500,000 International Units (IU)) was mixed with PMMA powder, whereby the composite powder was mixed with the DMAHDM-based liquid. The prepared specimens were tested for fungal adhesion testing (at days 1 and 30), impact strength and flexural strength. Oneway ANOVA post-hoc Tukey's test were used for statistical analysis.

Results: Statistical analysis for the adhesion assay revealed that the antifungal activities of unaged and aged specimens in experimental groups were statistically significant as compared to control group A. The groups containing DMAHDM with Nystatin have shown statistically reduced flexural strength. The impact strength test revealed that groups containing 20% DMAHDM alone and DMAHDM with Nystatin showed statistically reduced impact strength compared to the control group.

Conclusion: Antifungal activities of experimental PMMA resin was increased. The addition of DMAHDM alone in PMMA resin has no deleterious effects on impact and flexural strength, however, at higher concentration values were reduced.