{"title":"真空退火后Pt/Co多层膜矫顽力变化的研究","authors":"Ming Li, Zhihong Jiang, D. Shen","doi":"10.1117/12.248722","DOIUrl":null,"url":null,"abstract":"Effects of vacuum annealing on the coercivity in sputtered and evaporated Pt/Co multilayer films were detailedly investigated. Our experimental results showed that the coercivity experienced an initial increase and a subsequent decrease with the process of annealing. The saturation magnetization decreased slowly at initial annealing stage and then dropped drastically when the annealing temperature was further raised. The coercivity variation after vacuum annealing can be explained by the improvement of f.c.c. (111) texture and the reduction of Co layer thickness.","PeriodicalId":212484,"journal":{"name":"Optical Storage and Information Data Storage","volume":"10 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"1996-09-03","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Study on the coercivity variation in Pt/Co multilayer films after vacuum annealing\",\"authors\":\"Ming Li, Zhihong Jiang, D. Shen\",\"doi\":\"10.1117/12.248722\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Effects of vacuum annealing on the coercivity in sputtered and evaporated Pt/Co multilayer films were detailedly investigated. Our experimental results showed that the coercivity experienced an initial increase and a subsequent decrease with the process of annealing. The saturation magnetization decreased slowly at initial annealing stage and then dropped drastically when the annealing temperature was further raised. The coercivity variation after vacuum annealing can be explained by the improvement of f.c.c. (111) texture and the reduction of Co layer thickness.\",\"PeriodicalId\":212484,\"journal\":{\"name\":\"Optical Storage and Information Data Storage\",\"volume\":\"10 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1996-09-03\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Optical Storage and Information Data Storage\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1117/12.248722\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Optical Storage and Information Data Storage","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1117/12.248722","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Study on the coercivity variation in Pt/Co multilayer films after vacuum annealing
Effects of vacuum annealing on the coercivity in sputtered and evaporated Pt/Co multilayer films were detailedly investigated. Our experimental results showed that the coercivity experienced an initial increase and a subsequent decrease with the process of annealing. The saturation magnetization decreased slowly at initial annealing stage and then dropped drastically when the annealing temperature was further raised. The coercivity variation after vacuum annealing can be explained by the improvement of f.c.c. (111) texture and the reduction of Co layer thickness.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们