{"title":"脉冲电子束辐照过共晶矽明(al - 22 - 24wt .% Si)的结构和力学特性","authors":"E. Petrikova, Y. Ivanov, M. Rygina, Alexander Prudnicov, A. Teresov, M. Vorobyov","doi":"10.1109/EFRE47760.2020.9241979","DOIUrl":null,"url":null,"abstract":"Irradiation (“SOLO” setup, High-Current Electronics Institute SB RAS) of hypereutectic Al- (22–24) Si composition silumin samples with an intense pulsed electron beam was carried out. The formation of a multiphase submicron nanocrystalline structure is revealed. It was found that after modification, the hardness of silumin surface layer increases by more than 2 times. Tensile tests were carried out for flat proportional silumin samples in the initial and after irradiation states. An increase in the ductility of irradiated samples was demonstrated.","PeriodicalId":190249,"journal":{"name":"2020 7th International Congress on Energy Fluxes and Radiation Effects (EFRE)","volume":"41 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2020-09-14","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"The Structure and Mechanical Characteristics of the Hypereutectic Silumin (Al–22–24 wt.% Si), Irradiated by a Pulsed Electron Beam\",\"authors\":\"E. Petrikova, Y. Ivanov, M. Rygina, Alexander Prudnicov, A. Teresov, M. Vorobyov\",\"doi\":\"10.1109/EFRE47760.2020.9241979\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Irradiation (“SOLO” setup, High-Current Electronics Institute SB RAS) of hypereutectic Al- (22–24) Si composition silumin samples with an intense pulsed electron beam was carried out. The formation of a multiphase submicron nanocrystalline structure is revealed. It was found that after modification, the hardness of silumin surface layer increases by more than 2 times. Tensile tests were carried out for flat proportional silumin samples in the initial and after irradiation states. An increase in the ductility of irradiated samples was demonstrated.\",\"PeriodicalId\":190249,\"journal\":{\"name\":\"2020 7th International Congress on Energy Fluxes and Radiation Effects (EFRE)\",\"volume\":\"41 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2020-09-14\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"2020 7th International Congress on Energy Fluxes and Radiation Effects (EFRE)\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1109/EFRE47760.2020.9241979\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"2020 7th International Congress on Energy Fluxes and Radiation Effects (EFRE)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/EFRE47760.2020.9241979","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
摘要
用强脉冲电子束辐照(“SOLO”装置，High-Current Electronics Institute SB RAS)过共晶Al- (22-24) Si组成的硅明样品。揭示了多相亚微米纳米晶结构的形成。结果表明，改性后的硅敏表面层硬度提高了2倍以上。在辐照初始状态和辐照后状态下，对扁平比例硅明样品进行了拉伸试验。辐照样品的延展性有所增加。
The Structure and Mechanical Characteristics of the Hypereutectic Silumin (Al–22–24 wt.% Si), Irradiated by a Pulsed Electron Beam
Irradiation (“SOLO” setup, High-Current Electronics Institute SB RAS) of hypereutectic Al- (22–24) Si composition silumin samples with an intense pulsed electron beam was carried out. The formation of a multiphase submicron nanocrystalline structure is revealed. It was found that after modification, the hardness of silumin surface layer increases by more than 2 times. Tensile tests were carried out for flat proportional silumin samples in the initial and after irradiation states. An increase in the ductility of irradiated samples was demonstrated.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们