Activation Parameters of Linear Heating Crystallisation in Ni70.3Fe4.7Si15B10 Glassy Alloy Determined Using the Internal Friction Method

Using the internal friction method the effective activation energy E of crystallisation during linear heating is determined for the glassy alloy Ni70.3Fe4.7Si15B10. E values are obtained: from the Kissinger formula 2.49 eV, from the Augis-Bennett formula 2.51 eV. It is shown that this agreement is not accidental. The pre-exponential factor in the Arrhenius law K0 is calculated for four alloys investigated in the literature by the IF method. Values obtained lay in a very wide interval 1014 to 1027 s−1. It is shown that In K0 increases approximately linearly with E. Die effektive Aktivierungsenerigie E der Kristallisation wahrend linearer Erwarmung wird in amorphen Ni70,3Fe4,7Si15B10-Legierungen mit Hilfe der inneren Reibung untersucht. Fur E werden folgende Werte ermittelt: aus der Kissinger-Formel 2,49 eV, aus der Formel von Augis und Bennett 2,51 eV. Es wird gezeigt, das diese Ubereinstimmung nicht zufallig ist. Der praexponentielle Koeffizient K0 des Arrheniusgesetzes wird fur vier Legierungen, die in der Literatur mit der Methode der inneren Reibung untersucht wurden, berechnet. Die erhaltenen Werte liegen in einem sehr breiten Bereich, 1014 bis 1027 s−1. Es wird gezeigt, das ln K0 mit F fast linear ansteigt.