{"title":"共沉淀法合成纯和稀土金属Gd掺杂SnO2-CuO纳米颗粒及表征","authors":"L. Prakash, C. Tirupathi","doi":"10.30799/JNST.152.18040505","DOIUrl":null,"url":null,"abstract":"Pure and rare-earth metal Gd doped SnO2-CuO nanoparticles were successfully prepared from the starting materials SnCl2, CuCl2 and doping element gadolinium nitrate. Pure and Gd doped SnO2-CuO were synthesized by co-precipitation method. The samples were characterized using X-ray diffraction (XRD), Fourier transformed infrared spectroscopy (FTIR), UV-Vis, SEM, EDX and dielectric studies. The XRD analysis reveals that the rare-earth metal Gd dopants were substituted into rutile SnO2-CuO nanoparticles. Pure SnO2-CuO nanoparticles have an average crystallite size of 15 nm and rare-earth metal Gd doped SnO2-CuO nanoparticles have 18 nm. The average crystallite size of the sample increases when dopant was used and XRD peak intensity also increases when compared to pure SnO2-CuO nanoparticles. The optical absorption measurements exposed the nanometric size of the materials influences the energy band gap. Optical band gap was found to be 5.08 eV for pure SnO2-CuO nanoparticles and 5.14 eV for Gd doped SnO2-CuO nanoparticles. Surface morphology of pure and Gd doped SnO2-CuO nanoparticles annealed at 400 °C shows that most of the particles are rod shaped and hence it may have better sensitivity. Dielectric constant and dielectric loss decrease with increasing frequency at 100 °C and 200 °C. Doped samples show larger dielectric properties than pure SnO2-CuO nanoparticles.","PeriodicalId":268157,"journal":{"name":"Volume 4,Issue 5,2018","volume":"60 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2018-08-30","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"4","resultStr":"{\"title\":\"Synthesis and Characterization of Pure and Rare-Earth Metal Gd Doped SnO2-CuO Nanoparticles by Co-Precipitation Method\",\"authors\":\"L. Prakash, C. Tirupathi\",\"doi\":\"10.30799/JNST.152.18040505\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Pure and rare-earth metal Gd doped SnO2-CuO nanoparticles were successfully prepared from the starting materials SnCl2, CuCl2 and doping element gadolinium nitrate. Pure and Gd doped SnO2-CuO were synthesized by co-precipitation method. The samples were characterized using X-ray diffraction (XRD), Fourier transformed infrared spectroscopy (FTIR), UV-Vis, SEM, EDX and dielectric studies. The XRD analysis reveals that the rare-earth metal Gd dopants were substituted into rutile SnO2-CuO nanoparticles. Pure SnO2-CuO nanoparticles have an average crystallite size of 15 nm and rare-earth metal Gd doped SnO2-CuO nanoparticles have 18 nm. The average crystallite size of the sample increases when dopant was used and XRD peak intensity also increases when compared to pure SnO2-CuO nanoparticles. The optical absorption measurements exposed the nanometric size of the materials influences the energy band gap. Optical band gap was found to be 5.08 eV for pure SnO2-CuO nanoparticles and 5.14 eV for Gd doped SnO2-CuO nanoparticles. Surface morphology of pure and Gd doped SnO2-CuO nanoparticles annealed at 400 °C shows that most of the particles are rod shaped and hence it may have better sensitivity. Dielectric constant and dielectric loss decrease with increasing frequency at 100 °C and 200 °C. Doped samples show larger dielectric properties than pure SnO2-CuO nanoparticles.\",\"PeriodicalId\":268157,\"journal\":{\"name\":\"Volume 4,Issue 5,2018\",\"volume\":\"60 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2018-08-30\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"4\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Volume 4,Issue 5,2018\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.30799/JNST.152.18040505\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Volume 4,Issue 5,2018","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.30799/JNST.152.18040505","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Synthesis and Characterization of Pure and Rare-Earth Metal Gd Doped SnO2-CuO Nanoparticles by Co-Precipitation Method
Pure and rare-earth metal Gd doped SnO2-CuO nanoparticles were successfully prepared from the starting materials SnCl2, CuCl2 and doping element gadolinium nitrate. Pure and Gd doped SnO2-CuO were synthesized by co-precipitation method. The samples were characterized using X-ray diffraction (XRD), Fourier transformed infrared spectroscopy (FTIR), UV-Vis, SEM, EDX and dielectric studies. The XRD analysis reveals that the rare-earth metal Gd dopants were substituted into rutile SnO2-CuO nanoparticles. Pure SnO2-CuO nanoparticles have an average crystallite size of 15 nm and rare-earth metal Gd doped SnO2-CuO nanoparticles have 18 nm. The average crystallite size of the sample increases when dopant was used and XRD peak intensity also increases when compared to pure SnO2-CuO nanoparticles. The optical absorption measurements exposed the nanometric size of the materials influences the energy band gap. Optical band gap was found to be 5.08 eV for pure SnO2-CuO nanoparticles and 5.14 eV for Gd doped SnO2-CuO nanoparticles. Surface morphology of pure and Gd doped SnO2-CuO nanoparticles annealed at 400 °C shows that most of the particles are rod shaped and hence it may have better sensitivity. Dielectric constant and dielectric loss decrease with increasing frequency at 100 °C and 200 °C. Doped samples show larger dielectric properties than pure SnO2-CuO nanoparticles.