{"title":"RailTec系统:延长螺栓导轨的使用寿命","authors":"D. Archambeau","doi":"10.1109/RRCON.1989.77282","DOIUrl":null,"url":null,"abstract":"The author identifies the recent developments in the technology of fatigue enhancement of rail joints and summarizes the industry's testing results. Particular attention is given to the Railroad Cold Expansion System (RailTec). After years of testing, the split sleeve cold expansion system has been proven to enhance the life of bolted rail by minimizing bolt hole fatigue cracking. Using this process, there is an elimination or significant reduction of fatigue crack growth in the bolt hole region of the rail web. It is concluded that the RailTec system substantially reduces a major cause of rail failure and minimizes track inspection and maintenance costs.<<ETX>>","PeriodicalId":339427,"journal":{"name":"Proceedings., Technical Papers Presented at the IEEE/ASME Joint Railroad Conference","volume":"39 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"1989-04-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":"{\"title\":\"RailTec system: extending the life of bolted rail\",\"authors\":\"D. Archambeau\",\"doi\":\"10.1109/RRCON.1989.77282\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The author identifies the recent developments in the technology of fatigue enhancement of rail joints and summarizes the industry's testing results. Particular attention is given to the Railroad Cold Expansion System (RailTec). After years of testing, the split sleeve cold expansion system has been proven to enhance the life of bolted rail by minimizing bolt hole fatigue cracking. Using this process, there is an elimination or significant reduction of fatigue crack growth in the bolt hole region of the rail web. It is concluded that the RailTec system substantially reduces a major cause of rail failure and minimizes track inspection and maintenance costs.<<ETX>>\",\"PeriodicalId\":339427,\"journal\":{\"name\":\"Proceedings., Technical Papers Presented at the IEEE/ASME Joint Railroad Conference\",\"volume\":\"39 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1989-04-25\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"1\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Proceedings., Technical Papers Presented at the IEEE/ASME Joint Railroad Conference\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1109/RRCON.1989.77282\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Proceedings., Technical Papers Presented at the IEEE/ASME Joint Railroad Conference","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/RRCON.1989.77282","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
The author identifies the recent developments in the technology of fatigue enhancement of rail joints and summarizes the industry's testing results. Particular attention is given to the Railroad Cold Expansion System (RailTec). After years of testing, the split sleeve cold expansion system has been proven to enhance the life of bolted rail by minimizing bolt hole fatigue cracking. Using this process, there is an elimination or significant reduction of fatigue crack growth in the bolt hole region of the rail web. It is concluded that the RailTec system substantially reduces a major cause of rail failure and minimizes track inspection and maintenance costs.<>
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们