Fabrication and Characterization of Silicon Nanowires Heterojunction Solar Cell

Silicon nanowire arrays (SiNWs) are created utilizing the metal-assisted chemical etching method with an Ag metal as a catalyst and different etching time of 15, 30, and 60 minutes using n-Si (100). Physical properties such as structural, surface morphology, and optical properties of the prepared SiNWs are studied. The diameter of prepared SiNWs ranged from 20 to 280 nm, and the reflectance in the visible part of the wavelength spectrum was less than 1% for all prepared samples. The obtained energy gap of prepared SiNWs was around 2 eV, which is higher than the energy gap of bulk silicon. X-ray diffraction (XRD) has diffraction peaks at 68.70o for all prepared samples. The heterojunction solar cell was fabricated based on the n-SiNWs/ P3HT/PEDOT: PSS structure. The heterojunction solar cell produced for 60 minutes has the highest Jsc of 11.55 mA.cm-2 and a conversion efficiency of 0.93%. Based on SiNWs prepared for etching time of 15 min, the solar cell demonstrated Jsc and Voc of 2.73 mA/cm2 and 0.46 V, respectively, and a conversion efficiency of 0.34%.