Chemical, Thermal, and Mechanical Properties of Sulfur Polymer Composites Comprising Low-Value Fats and Pozzolan Additives

High sulfur-content materials (HSMs) formed via inverse vulcanization of elemental sulfur with animal fats and/or plant oils can exhibit remarkable mechanical strength and chemical resistance, sometimes superior to commercial building products. Adding pozzolan fine materials—fly ash (FA), silica fume (SF), ground granulated blast furnace slag (GGBFS), or metakaolin (MK)—can further improve HSM mechanical properties and stability. Herein, we detail nine materials comprised of rancidified chicken fat, elemental sulfur, and canola or sunflower oil (to yield CFS or GFS, respectively) and, with or without FA, SF, GGBFS, or MK. The base HSMs, CFS90 or GFS90, contained 90 wt% sulfur, 5 wt% chicken fat, and 5 wt% canola or sunflower oil, respectively. For each HSM/fine combination, the resulting material was prepared using a 95:5 mass input ratio of HSM/fine. No material exhibited water uptake >0.2 wt% after immersion in water for 24 h, significantly lower than the 28 wt% observed with ordinary Portland cement (OPC). Impressively, CFS90, GFS90, and all HSM/fine combinations exhibited compressive strength values 15% to 55% greater than OPC. After immersion in 0.5 M H2SO4, CFS90, GFS90, and its derivatives retained 90% to 171% of the initial strength of OPC, whereas OPC disintegrated under these conditions. CFS90, GFS90, and its derivatives collectively show promise as sustainable materials and materials with superior performance versus concrete.