氢对05Kh13N8M3铸马氏体钢静态抗裂性能的影响

IF 0.7 4区 材料科学 Q4 MATERIALS SCIENCE, CHARACTERIZATION & TESTING Strength of Materials Pub Date : 2023-12-04 DOI:10.1007/s11223-023-00581-w
O. I. Balytskyi, L. M. Ivaskevych
{"title":"氢对05Kh13N8M3铸马氏体钢静态抗裂性能的影响","authors":"O. I. Balytskyi, L. M. Ivaskevych","doi":"10.1007/s11223-023-00581-w","DOIUrl":null,"url":null,"abstract":"<p>The laws governing the influence of a hydrogen atmosphere at a pressure of up to 15 MPa with controlled total oxygen and water vapor content of up to 0.004 g/m<sup>3</sup> and pre-absorbed hydrogen on the strength and ductility characteristics, short-term and long-term static crack resistance of 05Kh13N8M3 cast martensitic steel (in wt.%: 0.045 C, 0.38 Si, 12.9 Cr, 2.69 Mo, 0.43 Mn, 7.8 Ni, 0.057 La) at room temperature were studied. After hydrogen pre-charging for 4 h at a temperature of 773 K and a pressure of 5, 10, and 15 MPa, the hydrogen content of the specimens determined with a LECO TCH 600 device by infrared adsorption with melting was 3.3, 4.9, and 7.6 ppm, respectively. It was found that under short-term loading, the intensity of the effect of hydrogen on the fracture toughness of steel increases with an increase in the absorbed hydrogen content, crack sharpness, and a decrease in the loading rate. At the maximum hydrogen concentration of 7.6 ppm and a tensile rate of 0.1 mm/min, the relative elongation, lateral contraction ratio of smooth 25 mm long cylindrical specimens with a test portion diameter of 5 mm and the critical stress intensity factor of beam specimens measuring 20×10×100 mm with a relative length of the pre-induced crack of <span>\\(\\upvarepsilon =\\)</span> 0.53 decrease almost twofold. At the same concentration, hydrogen does not affect the stress intensity factor of cracked specimens at a rate of 10 mm/min and specimens with a stress concentrator in the form of a notch with a tip radius of 0.065 mm at a rate of 0.1 mm/min. Under long-term static loading with a test duration of 300 h of double-cantilever beam specimens in the form of a rectangular plate 10 mm thick with milled grooves 3 mm deep and a tip angle of 60°, the threshold value of the stress intensity factor decreases. The rate of subcritical crack growth in the second portion of the hydrogen cracking diagram increases in proportion to the logarithm of hydrogen concentration.</p>","PeriodicalId":22007,"journal":{"name":"Strength of Materials","volume":null,"pages":null},"PeriodicalIF":0.7000,"publicationDate":"2023-12-04","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Effect of Hydrogen on the Static Crack Resistance of 05Kh13N8M3 Cast Martensitic Steel\",\"authors\":\"O. I. Balytskyi, L. M. Ivaskevych\",\"doi\":\"10.1007/s11223-023-00581-w\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p>The laws governing the influence of a hydrogen atmosphere at a pressure of up to 15 MPa with controlled total oxygen and water vapor content of up to 0.004 g/m<sup>3</sup> and pre-absorbed hydrogen on the strength and ductility characteristics, short-term and long-term static crack resistance of 05Kh13N8M3 cast martensitic steel (in wt.%: 0.045 C, 0.38 Si, 12.9 Cr, 2.69 Mo, 0.43 Mn, 7.8 Ni, 0.057 La) at room temperature were studied. After hydrogen pre-charging for 4 h at a temperature of 773 K and a pressure of 5, 10, and 15 MPa, the hydrogen content of the specimens determined with a LECO TCH 600 device by infrared adsorption with melting was 3.3, 4.9, and 7.6 ppm, respectively. It was found that under short-term loading, the intensity of the effect of hydrogen on the fracture toughness of steel increases with an increase in the absorbed hydrogen content, crack sharpness, and a decrease in the loading rate. At the maximum hydrogen concentration of 7.6 ppm and a tensile rate of 0.1 mm/min, the relative elongation, lateral contraction ratio of smooth 25 mm long cylindrical specimens with a test portion diameter of 5 mm and the critical stress intensity factor of beam specimens measuring 20×10×100 mm with a relative length of the pre-induced crack of <span>\\\\(\\\\upvarepsilon =\\\\)</span> 0.53 decrease almost twofold. At the same concentration, hydrogen does not affect the stress intensity factor of cracked specimens at a rate of 10 mm/min and specimens with a stress concentrator in the form of a notch with a tip radius of 0.065 mm at a rate of 0.1 mm/min. Under long-term static loading with a test duration of 300 h of double-cantilever beam specimens in the form of a rectangular plate 10 mm thick with milled grooves 3 mm deep and a tip angle of 60°, the threshold value of the stress intensity factor decreases. The rate of subcritical crack growth in the second portion of the hydrogen cracking diagram increases in proportion to the logarithm of hydrogen concentration.</p>\",\"PeriodicalId\":22007,\"journal\":{\"name\":\"Strength of Materials\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.7000,\"publicationDate\":\"2023-12-04\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Strength of Materials\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1007/s11223-023-00581-w\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MATERIALS SCIENCE, CHARACTERIZATION & TESTING\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Strength of Materials","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1007/s11223-023-00581-w","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, CHARACTERIZATION & TESTING","Score":null,"Total":0}
引用次数: 0

摘要

研究了压力为15 MPa、总氧和水蒸气含量控制在0.004 g/m3以下和预吸收氢对05Kh13N8M3铸造马氏体钢(wt)强度和延展性特性、短期和长期静态抗裂性能的影响规律。%: 0.045 C, 0.38 Si, 12.9 Cr, 2.69 Mo, 0.43 Mn, 7.8 Ni, 0.057 La) at room temperature were studied. After hydrogen pre-charging for 4 h at a temperature of 773 K and a pressure of 5, 10, and 15 MPa, the hydrogen content of the specimens determined with a LECO TCH 600 device by infrared adsorption with melting was 3.3, 4.9, and 7.6 ppm, respectively. It was found that under short-term loading, the intensity of the effect of hydrogen on the fracture toughness of steel increases with an increase in the absorbed hydrogen content, crack sharpness, and a decrease in the loading rate. At the maximum hydrogen concentration of 7.6 ppm and a tensile rate of 0.1 mm/min, the relative elongation, lateral contraction ratio of smooth 25 mm long cylindrical specimens with a test portion diameter of 5 mm and the critical stress intensity factor of beam specimens measuring 20×10×100 mm with a relative length of the pre-induced crack of \(\upvarepsilon =\) 0.53 decrease almost twofold. At the same concentration, hydrogen does not affect the stress intensity factor of cracked specimens at a rate of 10 mm/min and specimens with a stress concentrator in the form of a notch with a tip radius of 0.065 mm at a rate of 0.1 mm/min. Under long-term static loading with a test duration of 300 h of double-cantilever beam specimens in the form of a rectangular plate 10 mm thick with milled grooves 3 mm deep and a tip angle of 60°, the threshold value of the stress intensity factor decreases. The rate of subcritical crack growth in the second portion of the hydrogen cracking diagram increases in proportion to the logarithm of hydrogen concentration.
本文章由计算机程序翻译,如有差异,请以英文原文为准。

摘要图片

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Effect of Hydrogen on the Static Crack Resistance of 05Kh13N8M3 Cast Martensitic Steel

The laws governing the influence of a hydrogen atmosphere at a pressure of up to 15 MPa with controlled total oxygen and water vapor content of up to 0.004 g/m3 and pre-absorbed hydrogen on the strength and ductility characteristics, short-term and long-term static crack resistance of 05Kh13N8M3 cast martensitic steel (in wt.%: 0.045 C, 0.38 Si, 12.9 Cr, 2.69 Mo, 0.43 Mn, 7.8 Ni, 0.057 La) at room temperature were studied. After hydrogen pre-charging for 4 h at a temperature of 773 K and a pressure of 5, 10, and 15 MPa, the hydrogen content of the specimens determined with a LECO TCH 600 device by infrared adsorption with melting was 3.3, 4.9, and 7.6 ppm, respectively. It was found that under short-term loading, the intensity of the effect of hydrogen on the fracture toughness of steel increases with an increase in the absorbed hydrogen content, crack sharpness, and a decrease in the loading rate. At the maximum hydrogen concentration of 7.6 ppm and a tensile rate of 0.1 mm/min, the relative elongation, lateral contraction ratio of smooth 25 mm long cylindrical specimens with a test portion diameter of 5 mm and the critical stress intensity factor of beam specimens measuring 20×10×100 mm with a relative length of the pre-induced crack of \(\upvarepsilon =\) 0.53 decrease almost twofold. At the same concentration, hydrogen does not affect the stress intensity factor of cracked specimens at a rate of 10 mm/min and specimens with a stress concentrator in the form of a notch with a tip radius of 0.065 mm at a rate of 0.1 mm/min. Under long-term static loading with a test duration of 300 h of double-cantilever beam specimens in the form of a rectangular plate 10 mm thick with milled grooves 3 mm deep and a tip angle of 60°, the threshold value of the stress intensity factor decreases. The rate of subcritical crack growth in the second portion of the hydrogen cracking diagram increases in proportion to the logarithm of hydrogen concentration.

求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Strength of Materials
Strength of Materials MATERIALS SCIENCE, CHARACTERIZATION & TESTING-
CiteScore
1.20
自引率
14.30%
发文量
89
审稿时长
6-12 weeks
期刊介绍: Strength of Materials focuses on the strength of materials and structural components subjected to different types of force and thermal loadings, the limiting strength criteria of structures, and the theory of strength of structures. Consideration is given to actual operating conditions, problems of crack resistance and theories of failure, the theory of oscillations of real mechanical systems, and calculations of the stress-strain state of structural components.
期刊最新文献
Simulation Analysis of Mechanical Properties of DC Transmission Lines Under Mountain Fire Condition Eulerian Formulation of the Constitutive Relation for an Electro-Magneto-Elastic Material Class Impact Damage Prediction of Carbon Fiber Foam Sandwich Structure Based on the Hashin Failure Criterion Simulation of Low-Temperature Localized Serrated Deformation of Structural Materials in Liquid Helium Under Different Loading Modes and Potential Energy Accumulation Effect of Structural Anisotropy on a Fracture Mode of Ferromagnetic Steels Under Cyclic Loading
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1