{"title":"基于高岭土铬酸盐骨料的低水泥耐火混凝土具有更好的施工性","authors":"V. A. Abyzov, I. E. Leshchenko","doi":"10.17073/1683-4518-2023-8-44-47","DOIUrl":null,"url":null,"abstract":"The results of the development of low-cement refractory concrete (LCC) based on a filler made of kaolin chamotte with a maximum application temperature of 1500 o C are presented. It is shown that in order to obtain high rates of workability, narrow fractions of filler with reduced water demand should be used. A comparative analysis of the effectiveness of superplasticizer additives has been carried out, their effect on the properties of kaolin chamotte-based LCC has been evaluated. It is established that the use of kaolin chamotte provides high strength of refractory concrete (more than 50 MPa after drying and first heating to operating temperatures).","PeriodicalId":19463,"journal":{"name":"NOVYE OGNEUPORY (NEW REFRACTORIES)","volume":"19 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2023-11-30","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Low-cement refractory concrete based on kaolin chamotte aggregate with improved workability\",\"authors\":\"V. A. Abyzov, I. E. Leshchenko\",\"doi\":\"10.17073/1683-4518-2023-8-44-47\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The results of the development of low-cement refractory concrete (LCC) based on a filler made of kaolin chamotte with a maximum application temperature of 1500 o C are presented. It is shown that in order to obtain high rates of workability, narrow fractions of filler with reduced water demand should be used. A comparative analysis of the effectiveness of superplasticizer additives has been carried out, their effect on the properties of kaolin chamotte-based LCC has been evaluated. It is established that the use of kaolin chamotte provides high strength of refractory concrete (more than 50 MPa after drying and first heating to operating temperatures).\",\"PeriodicalId\":19463,\"journal\":{\"name\":\"NOVYE OGNEUPORY (NEW REFRACTORIES)\",\"volume\":\"19 1\",\"pages\":\"\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2023-11-30\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"NOVYE OGNEUPORY (NEW REFRACTORIES)\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.17073/1683-4518-2023-8-44-47\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"NOVYE OGNEUPORY (NEW REFRACTORIES)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.17073/1683-4518-2023-8-44-47","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Low-cement refractory concrete based on kaolin chamotte aggregate with improved workability
The results of the development of low-cement refractory concrete (LCC) based on a filler made of kaolin chamotte with a maximum application temperature of 1500 o C are presented. It is shown that in order to obtain high rates of workability, narrow fractions of filler with reduced water demand should be used. A comparative analysis of the effectiveness of superplasticizer additives has been carried out, their effect on the properties of kaolin chamotte-based LCC has been evaluated. It is established that the use of kaolin chamotte provides high strength of refractory concrete (more than 50 MPa after drying and first heating to operating temperatures).
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们