Forging Treatment Realized the Isotropic Microstructure and Properties of Selective Laser Melting GH3536

The anisotropy of mechanical properties in SLMed alloy is very important. In order to realize the homogeneity of the microstructure and mechanical properties of GH3536 alloy prepared by selective laser melting (SLM), the as-deposited samples were treated by hot isostatic pressing and then forged at different temperatures. The microstructure, grain size, room- and high- temperature tensile properties, and endurance properties of the samples were studied. The results showed that the microstructure of the sample was mainly equiaxed austenite phase, and granular carbides were precipitated inside the grains after forging treatment, resulting in the anisotropy of the sample almost disappearing. The grain boundary phase difference distribution was most concentrated at 60°. The grain size was less than 10 μm, and a large number of twins were formed. With the increase in forging temperature, the yield strength, tensile strength, and contraction of area of the samples changed little, and the properties parallel to the z-axis (parallel samples) and vertical to the z-axis (vertical samples) were almost the same. In particular, the yield strength, tensile strength, and contraction of area in the transverse and vertical samples were almost at the same level. Judging from the elongation after fracture and the contraction of area, the properties of the samples showed characteristics of anisotropy after a high temperature endurance test.