Microstructure and dielectric properties of low-temperature sintered MgO-based ceramics at millimeter wave and terahertz frequencies

Low-temperature co-fired ceramics (LTCC) applied in millimeter/microwave and terahertz frequencies (5G/6G) have attracted a lot of attention recently. In this study, MgO-based dielectric ceramics were successfully sintered at 950∘C with the sintering aids: x wt.% of LiF fluoride ([Formula: see text], 4, 6, 8, 10) and 0.5[Formula: see text]wt.% of BBSZ (Bi2O3–B2O3–SiO2–ZnO) glass. BBSZ glass was introduced as another sintering aid to facilitate the sintering and densification. Crystalline structure and micro-morphology were investigated and analyzed. Dielectric properties ([Formula: see text], [Formula: see text], [Formula: see text]) at millimeter/microwave and terahertz wave frequencies were also studied. The ionic characteristics of Mg–O bond ([Formula: see text]), the lattice energy (U) and the bond energy (E) were calculated and analyzed. It is suggested that the optimal [Formula: see text], where [Formula: see text], [Formula: see text][Formula: see text]GHz (@12[Formula: see text]GHz) and [Formula: see text][Formula: see text]ppm/∘C at millimeter/microwave range. When the frequency was up to terahertz (1.0[Formula: see text]THz), the [Formula: see text] values were 8.8–9.35 and the tan[Formula: see text] were [Formula: see text]–[Formula: see text]. The experimental results indicated that the low-temperature sintered MgO-based ceramics have potential for millimeter/microwave and terahertz communication applications.