H. H. Veselivska, I. M. Pohrelyuk, R. V. Proskurnyak, O. S. Kuprin
{"title":"不同表面条件下 VT1-0 钛上沉积的 TiN 涂层的附着强度","authors":"H. H. Veselivska, I. M. Pohrelyuk, R. V. Proskurnyak, O. S. Kuprin","doi":"10.1007/s11003-024-00800-y","DOIUrl":null,"url":null,"abstract":"<p>The TiN coating obtained by vacuum-arc spraying on the surface of commercially pure VT1-0 titanium and thermodiffusion saturation in a nitrogen atmosphere was studied. The coating was evaluated by thickness, phase composition, surface roughness, microhardness, and adhesive strength. Rockwell adhesion tests showed that the TiN coatings applied to both untreated and pre-nitrided titanium meet the HF2 adhesion level accepted for commercial application on products.</p>","PeriodicalId":18230,"journal":{"name":"Materials Science","volume":"48 1","pages":""},"PeriodicalIF":0.7000,"publicationDate":"2024-04-22","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Adhesion Strength of TiN Coatings Deposited on VT1-0 Titanium with Different Surface Conditions\",\"authors\":\"H. H. Veselivska, I. M. Pohrelyuk, R. V. Proskurnyak, O. S. Kuprin\",\"doi\":\"10.1007/s11003-024-00800-y\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p>The TiN coating obtained by vacuum-arc spraying on the surface of commercially pure VT1-0 titanium and thermodiffusion saturation in a nitrogen atmosphere was studied. The coating was evaluated by thickness, phase composition, surface roughness, microhardness, and adhesive strength. Rockwell adhesion tests showed that the TiN coatings applied to both untreated and pre-nitrided titanium meet the HF2 adhesion level accepted for commercial application on products.</p>\",\"PeriodicalId\":18230,\"journal\":{\"name\":\"Materials Science\",\"volume\":\"48 1\",\"pages\":\"\"},\"PeriodicalIF\":0.7000,\"publicationDate\":\"2024-04-22\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materials Science\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1007/s11003-024-00800-y\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Science","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1007/s11003-024-00800-y","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0
摘要
研究了在商业纯钛 VT1-0 表面进行真空电弧喷涂并在氮气环境中进行热扩散饱和而获得的 TiN 涂层。涂层的厚度、相组成、表面粗糙度、显微硬度和粘合强度都得到了评估。洛氏硬度附着力测试表明，应用于未处理钛和预氮化钛的 TiN 涂层都达到了产品商业应用所认可的 HF2 附着力水平。
Adhesion Strength of TiN Coatings Deposited on VT1-0 Titanium with Different Surface Conditions
The TiN coating obtained by vacuum-arc spraying on the surface of commercially pure VT1-0 titanium and thermodiffusion saturation in a nitrogen atmosphere was studied. The coating was evaluated by thickness, phase composition, surface roughness, microhardness, and adhesive strength. Rockwell adhesion tests showed that the TiN coatings applied to both untreated and pre-nitrided titanium meet the HF2 adhesion level accepted for commercial application on products.
期刊介绍：
Materials Science reports on current research into such problems as cracking, fatigue and fracture, especially in active environments as well as corrosion and anticorrosion protection of structural metallic and polymer materials, and the development of new materials.