Electrochemical Properties of Nickel-Titanium Rotary Endodontic Instruments

Introduction

Nickel-titanium rotary endodontic files have been commercially available for decades, but more recent innovations have introduced heat-treated and surface-treated files. This study investigated the corrosion properties of various nickel-titanium files in normal saline and sodium hypochlorite (NaOCl).

Methods

Ten different file brands of size 40 with a 0.04 taper were subjected to electrochemical testing in 0.9% NaCl (saline) and 5.25% NaOCl at room temperature. The Open Circuit Potential (OCP) was observed for 1 hour followed by a cyclic polarization test from −300 to 700 mV and back to −300 mV (vs OCP). Nonparametric ANOVA and a pairwise comparison (P < .05) were used for statistical analysis of the OCP at 1 hour and the corrosion current (Icorr) obtained via the cyclic polarization test.

Results

Significant differences (P < .05) were found between files with respect to OCP and Icorr in both solutions. Nine files exhibited significantly greater (P < .05) Icorrs in NaOCl than in saline. Conversely, pitting corrosion was observed in the saline solution but not NaOCl. Weak and/or moderate correlations existed between OCP and Icorr measures in the 2 solutions.

Conclusion

Significant differences in electrochemical properties were observed among the 10 brands of files. Overall, there was not a clear trend between conventional, heat-treated, or surface-treated files among OCP or Icorr in either solution.