Slow hole diffusion limits the efficiency of p-type dye-sensitized solar cells based on the P1 dye†

NiO electrodes are widely applied in p-type dye-sensitized solar cells (DSSCs) and photoelectrochemical cells, but due to excessive charge recombination, the efficiencies of these devices are still too low for commercial applications. To understand which factors induce charge recombination, we studied electrodes with a varying number of NiO layers in benchmark P1 p-DSSCs. We obtained the most efficient DSSCs with four layers of NiO (0.134%), and further insights into this optimum were obtained via dye loading studies and in operando photoelectrochemical immittance spectroscopy. These results revealed that more NiO layers led to an increasing light harvesting efficiency (η_LH), but a decreasing hole collection efficiency (η_CC), giving rise to the maximum efficiency at four NiO layers. The decreasing η_CC with more NiO layers is caused by longer hole collection times, which ultimately limits the overall efficiency. Notably, the recombination rates were independent of the number of NiO layers, and similar to those observed in the more efficient n-type DSSC analogues, but hole collection was an order of magnitude slower. Therefore, with more NiO layers, the beneficial increase in η_LH can no longer counteract the decrease in η_CC due to slow hole collection, resulting in the overall efficiency of the solar cells to maximize at four NiO layers.