Sunay Bebekoğlu, Ahmet Topuz, Esin Çakır, Abdülhamit Adsoy, Turgay Yıldıran
{"title":"为高速列车开发烧结衬里","authors":"Sunay Bebekoğlu, Ahmet Topuz, Esin Çakır, Abdülhamit Adsoy, Turgay Yıldıran","doi":"10.1515/mt-2023-0422","DOIUrl":null,"url":null,"abstract":"Abstract In this study, brake linings with Cu (copper)-based and Cu-10Sn (bronze)-based matrix structures have been developed and produced by the powder metallurgy method using sinter metal technology for use in high-speed trains. The developed linings were compared with commercial high-speed train linings. Firstly, the mixing process was carried out in a Turbulo 3V three-dimensional mixer for 4.5 h at 50 rpm. The pressing process was performed at room temperature, under the pressure of 350–450 MPa, and the sintering temperature for Cu-based linings was 1,000 °C, while for Cu-10Sn-based linings, it was 800 °C. After the pressing and sintering processes, lining sample density calculations were conducted, and hardness tests were carried out in the Rockwell L scale. Shear strength tests, friction coefficient, and wear tests were conducted according to SAE J 661 standards. It was observed that sinter metal brake linings with Cu and Cu-10Sn main matrix structures showed similar properties and met the technical requirements. It was determined that the developed production prescriptions are promising for industrial production and patent studies.","PeriodicalId":18231,"journal":{"name":"Materials Testing","volume":null,"pages":null},"PeriodicalIF":2.4000,"publicationDate":"2024-07-08","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Development of sinter linings for high-speed trains\",\"authors\":\"Sunay Bebekoğlu, Ahmet Topuz, Esin Çakır, Abdülhamit Adsoy, Turgay Yıldıran\",\"doi\":\"10.1515/mt-2023-0422\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Abstract In this study, brake linings with Cu (copper)-based and Cu-10Sn (bronze)-based matrix structures have been developed and produced by the powder metallurgy method using sinter metal technology for use in high-speed trains. The developed linings were compared with commercial high-speed train linings. Firstly, the mixing process was carried out in a Turbulo 3V three-dimensional mixer for 4.5 h at 50 rpm. The pressing process was performed at room temperature, under the pressure of 350–450 MPa, and the sintering temperature for Cu-based linings was 1,000 °C, while for Cu-10Sn-based linings, it was 800 °C. After the pressing and sintering processes, lining sample density calculations were conducted, and hardness tests were carried out in the Rockwell L scale. Shear strength tests, friction coefficient, and wear tests were conducted according to SAE J 661 standards. It was observed that sinter metal brake linings with Cu and Cu-10Sn main matrix structures showed similar properties and met the technical requirements. It was determined that the developed production prescriptions are promising for industrial production and patent studies.\",\"PeriodicalId\":18231,\"journal\":{\"name\":\"Materials Testing\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":2.4000,\"publicationDate\":\"2024-07-08\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materials Testing\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1515/mt-2023-0422\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"MATERIALS SCIENCE, CHARACTERIZATION & TESTING\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Testing","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1515/mt-2023-0422","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"MATERIALS SCIENCE, CHARACTERIZATION & TESTING","Score":null,"Total":0}
Development of sinter linings for high-speed trains
Abstract In this study, brake linings with Cu (copper)-based and Cu-10Sn (bronze)-based matrix structures have been developed and produced by the powder metallurgy method using sinter metal technology for use in high-speed trains. The developed linings were compared with commercial high-speed train linings. Firstly, the mixing process was carried out in a Turbulo 3V three-dimensional mixer for 4.5 h at 50 rpm. The pressing process was performed at room temperature, under the pressure of 350–450 MPa, and the sintering temperature for Cu-based linings was 1,000 °C, while for Cu-10Sn-based linings, it was 800 °C. After the pressing and sintering processes, lining sample density calculations were conducted, and hardness tests were carried out in the Rockwell L scale. Shear strength tests, friction coefficient, and wear tests were conducted according to SAE J 661 standards. It was observed that sinter metal brake linings with Cu and Cu-10Sn main matrix structures showed similar properties and met the technical requirements. It was determined that the developed production prescriptions are promising for industrial production and patent studies.
期刊介绍:
Materials Testing is a SCI-listed English language journal dealing with all aspects of material and component testing with a special focus on transfer between laboratory research into industrial application. The journal provides first-hand information on non-destructive, destructive, optical, physical and chemical test procedures. It contains exclusive articles which are peer-reviewed applying respectively high international quality criterions.