二氧化锆纳米添加剂对莫来石-刚玉特性的影响

IF 0.6 4区 物理与天体物理 Q4 PHYSICS, APPLIED Low Temperature Physics Pub Date : 2024-07-19 DOI:10.1063/10.0026282
V. P. Nerubatskyi, E. S. Hevorkian, R. V. Vovk, Z. Krzysiak, H. L. Komarova
{"title":"二氧化锆纳米添加剂对莫来石-刚玉特性的影响","authors":"V. P. Nerubatskyi, E. S. Hevorkian, R. V. Vovk, Z. Krzysiak, H. L. Komarova","doi":"10.1063/10.0026282","DOIUrl":null,"url":null,"abstract":"The paper analyzes the effect of nanoadditives of zirconium dioxide, partially stabilized by Y2O3, on the Al2O3–SiO2 matrix during hot pressing by the electroconsolidation method. The microstructure obtained at different compositions and sintering modes is studied. It was established that the introduction of nanopowder ZrO2–3 mol % Y2O3 increases the crack resistance of sintered samples not only due to the transformation of the tetragonal phase to the monoclinic phase, but also due to the formation of a solid solution with aluminum oxide at the interphase boundaries. Starting from a temperature of 1400 °C, complete densification occurs with the formation of nonporous composites while preserving the nanostructure. At this temperature, the formation of mullite with cristobalite phases also begins. The high value of thermocycles makes it possible to use this composite material as a cryogenic one. The fabrication of mullite-corundum composites with additions of ZrO2–3 mol % Y2O3 nanopowders via the method of electrosolidification has enabled the attainment of high fracture toughness, K1C = 14.5 MPa⋅m1/2, and hardness HV10 = 14 GPa. These results evidence excellent mechanical properties, thereby expanding the potential applications of this material.","PeriodicalId":18077,"journal":{"name":"Low Temperature Physics","volume":"46 1","pages":""},"PeriodicalIF":0.6000,"publicationDate":"2024-07-19","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"The influence of zirconium dioxide nanoadditives on the properties of mullite-corundum\",\"authors\":\"V. P. Nerubatskyi, E. S. Hevorkian, R. V. Vovk, Z. Krzysiak, H. L. Komarova\",\"doi\":\"10.1063/10.0026282\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The paper analyzes the effect of nanoadditives of zirconium dioxide, partially stabilized by Y2O3, on the Al2O3–SiO2 matrix during hot pressing by the electroconsolidation method. The microstructure obtained at different compositions and sintering modes is studied. It was established that the introduction of nanopowder ZrO2–3 mol % Y2O3 increases the crack resistance of sintered samples not only due to the transformation of the tetragonal phase to the monoclinic phase, but also due to the formation of a solid solution with aluminum oxide at the interphase boundaries. Starting from a temperature of 1400 °C, complete densification occurs with the formation of nonporous composites while preserving the nanostructure. At this temperature, the formation of mullite with cristobalite phases also begins. The high value of thermocycles makes it possible to use this composite material as a cryogenic one. The fabrication of mullite-corundum composites with additions of ZrO2–3 mol % Y2O3 nanopowders via the method of electrosolidification has enabled the attainment of high fracture toughness, K1C = 14.5 MPa⋅m1/2, and hardness HV10 = 14 GPa. These results evidence excellent mechanical properties, thereby expanding the potential applications of this material.\",\"PeriodicalId\":18077,\"journal\":{\"name\":\"Low Temperature Physics\",\"volume\":\"46 1\",\"pages\":\"\"},\"PeriodicalIF\":0.6000,\"publicationDate\":\"2024-07-19\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Low Temperature Physics\",\"FirstCategoryId\":\"101\",\"ListUrlMain\":\"https://doi.org/10.1063/10.0026282\",\"RegionNum\":4,\"RegionCategory\":\"物理与天体物理\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"PHYSICS, APPLIED\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Low Temperature Physics","FirstCategoryId":"101","ListUrlMain":"https://doi.org/10.1063/10.0026282","RegionNum":4,"RegionCategory":"物理与天体物理","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"PHYSICS, APPLIED","Score":null,"Total":0}
引用次数: 0

摘要

本文分析了电固相法热压过程中部分由 Y2O3 稳定的纳米二氧化锆添加剂对 Al2O3-SiO2 基体的影响。研究了不同成分和烧结模式下获得的微观结构。结果表明,纳米粉体 ZrO2-3 mol % Y2O3 的引入不仅增加了烧结样品的抗裂性,这不仅是由于四方相转变为单斜相,还由于在相间边界形成了氧化铝固溶体。从 1400 °C 的温度开始,在保留纳米结构的同时,完全致密化并形成无孔复合材料。在此温度下,还开始形成莫来石和脆闪石相。高热循环值使得这种复合材料可以用作低温材料。通过电固化方法制造的莫来石-刚玉复合材料中添加了 ZrO2-3 mol % Y2O3 纳米粉末,从而获得了较高的断裂韧性 K1C = 14.5 MPa-m1/2,硬度 HV10 = 14 GPa。这些结果证明了该材料具有优异的机械性能,从而拓展了其潜在的应用领域。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
The influence of zirconium dioxide nanoadditives on the properties of mullite-corundum
The paper analyzes the effect of nanoadditives of zirconium dioxide, partially stabilized by Y2O3, on the Al2O3–SiO2 matrix during hot pressing by the electroconsolidation method. The microstructure obtained at different compositions and sintering modes is studied. It was established that the introduction of nanopowder ZrO2–3 mol % Y2O3 increases the crack resistance of sintered samples not only due to the transformation of the tetragonal phase to the monoclinic phase, but also due to the formation of a solid solution with aluminum oxide at the interphase boundaries. Starting from a temperature of 1400 °C, complete densification occurs with the formation of nonporous composites while preserving the nanostructure. At this temperature, the formation of mullite with cristobalite phases also begins. The high value of thermocycles makes it possible to use this composite material as a cryogenic one. The fabrication of mullite-corundum composites with additions of ZrO2–3 mol % Y2O3 nanopowders via the method of electrosolidification has enabled the attainment of high fracture toughness, K1C = 14.5 MPa⋅m1/2, and hardness HV10 = 14 GPa. These results evidence excellent mechanical properties, thereby expanding the potential applications of this material.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Low Temperature Physics
Low Temperature Physics 物理-物理:应用
CiteScore
1.20
自引率
25.00%
发文量
138
审稿时长
3 months
期刊介绍: Guided by an international editorial board, Low Temperature Physics (LTP) communicates the results of important experimental and theoretical studies conducted at low temperatures. LTP offers key work in such areas as superconductivity, magnetism, lattice dynamics, quantum liquids and crystals, cryocrystals, low-dimensional and disordered systems, electronic properties of normal metals and alloys, and critical phenomena. The journal publishes original articles on new experimental and theoretical results as well as review articles, brief communications, memoirs, and biographies. Low Temperature Physics, a translation of the copyrighted Journal FIZIKA NIZKIKH TEMPERATUR, is a monthly journal containing English reports of current research in the field of the low temperature physics. The translation began with the 1975 issues. One volume is published annually beginning with the January issues.
期刊最新文献
Revisiting structural, vibrational, and photochemical data of matrix-isolated simple hydantoins — Common features and substituent effects Conformers of valeric acid: Matrix isolation infrared spectroscopy study Helium 1s photoemission and photon stimulated desorption of He+ ions by double excitations from adsorbed helium layers: Zero-point motion and matrix effects Characterization of H–π and CH–O structures of the 1:1 methanol-benzene complex using matrix isolation infrared spectroscopy Linearly polarized luminescence of polyyne molecules aligned in PVA films
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1