通过溶胶-凝胶工艺制备伴有相分离的大孔磷酸铁锰锂/碳复合材料

IF 2.5 4区 材料科学 Q2 CHEMISTRY, APPLIED Journal of Porous Materials Pub Date : 2024-07-25 DOI:10.1007/s10934-024-01666-w
Zhizhen Zhang, Xin Ouyang, Junzhang Wang, Xingzhong Guo
{"title":"通过溶胶-凝胶工艺制备伴有相分离的大孔磷酸铁锰锂/碳复合材料","authors":"Zhizhen Zhang,&nbsp;Xin Ouyang,&nbsp;Junzhang Wang,&nbsp;Xingzhong Guo","doi":"10.1007/s10934-024-01666-w","DOIUrl":null,"url":null,"abstract":"<div><p>Macroporous lithium manganese iron phosphate/carbon (LiFe<sub>0.9</sub>Mn<sub>0.1</sub>PO<sub>4</sub>/C) has been successfully synthesized via a sol-gel process accompanied by phase separation. Poly (ethylene oxide) (PEO) acts as a phase separation inducer, while polyvinylpyrrolidone (PVP) synergistically regulates the morphology of the gel skeleton and serves as a reducing agent. Propylene oxide (PO) works as a proton scavenger to initiate the homogeneous gelation and modify the macrostructure. An appropriate amount of PEO, PVP and PO led to the formation of xerogel monoliths characterized by a three-dimensional co-continuous skeleton and interconnected macropores. The amorphous xerogel upon heat treatment at 400 °C for 2 h under a N<sub>2</sub> atmosphere, formed carbon-coated LiFe<sub>0.9</sub>Mn<sub>0.1</sub>PO<sub>4</sub>/C crystals with excellent crystallinity and uniform elemental distribution. The resultant macroporous LFMP/C has a discharge capacity of 113.43 mA h g<sup>− 1</sup> at 0.1 C, with a first coulombic efficiency of 90.1% and excellent capacity recovery rate after high-rate tests.</p></div>","PeriodicalId":660,"journal":{"name":"Journal of Porous Materials","volume":null,"pages":null},"PeriodicalIF":2.5000,"publicationDate":"2024-07-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://link.springer.com/content/pdf/10.1007/s10934-024-01666-w.pdf","citationCount":"0","resultStr":"{\"title\":\"Preparation of macroporous lithium iron manganese phosphate/carbon composites via sol-gel process accompanied by phase separation\",\"authors\":\"Zhizhen Zhang,&nbsp;Xin Ouyang,&nbsp;Junzhang Wang,&nbsp;Xingzhong Guo\",\"doi\":\"10.1007/s10934-024-01666-w\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>Macroporous lithium manganese iron phosphate/carbon (LiFe<sub>0.9</sub>Mn<sub>0.1</sub>PO<sub>4</sub>/C) has been successfully synthesized via a sol-gel process accompanied by phase separation. Poly (ethylene oxide) (PEO) acts as a phase separation inducer, while polyvinylpyrrolidone (PVP) synergistically regulates the morphology of the gel skeleton and serves as a reducing agent. Propylene oxide (PO) works as a proton scavenger to initiate the homogeneous gelation and modify the macrostructure. An appropriate amount of PEO, PVP and PO led to the formation of xerogel monoliths characterized by a three-dimensional co-continuous skeleton and interconnected macropores. The amorphous xerogel upon heat treatment at 400 °C for 2 h under a N<sub>2</sub> atmosphere, formed carbon-coated LiFe<sub>0.9</sub>Mn<sub>0.1</sub>PO<sub>4</sub>/C crystals with excellent crystallinity and uniform elemental distribution. The resultant macroporous LFMP/C has a discharge capacity of 113.43 mA h g<sup>− 1</sup> at 0.1 C, with a first coulombic efficiency of 90.1% and excellent capacity recovery rate after high-rate tests.</p></div>\",\"PeriodicalId\":660,\"journal\":{\"name\":\"Journal of Porous Materials\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":2.5000,\"publicationDate\":\"2024-07-25\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://link.springer.com/content/pdf/10.1007/s10934-024-01666-w.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Porous Materials\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://link.springer.com/article/10.1007/s10934-024-01666-w\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"CHEMISTRY, APPLIED\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Porous Materials","FirstCategoryId":"88","ListUrlMain":"https://link.springer.com/article/10.1007/s10934-024-01666-w","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"CHEMISTRY, APPLIED","Score":null,"Total":0}
引用次数: 0

摘要

通过伴随相分离的溶胶-凝胶工艺,成功合成了大孔磷酸锰铁锂/碳(LiFe0.9Mn0.1PO4/C)。聚环氧乙烷(PEO)作为相分离诱导剂,而聚乙烯吡咯烷酮(PVP)则协同调节凝胶骨架的形态并作为还原剂。环氧丙烷(PO)作为质子清除剂,可启动均匀凝胶化并改变宏观结构。适量的 PEO、PVP 和 PO 可形成以三维共连续骨架和相互连接的大孔为特征的气凝胶单体。无定形的 xerogel 在氮气环境下于 400 °C 热处理 2 小时后,形成了碳包覆的 LiFe0.9Mn0.1PO4/C 晶体,具有极佳的结晶性和均匀的元素分布。由此产生的大孔 LFMP/C 在 0.1 C 下的放电容量为 113.43 mA h g- 1,首次库仑效率为 90.1%,并且在高速率测试后具有极佳的容量恢复率。
本文章由计算机程序翻译,如有差异,请以英文原文为准。

摘要图片

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Preparation of macroporous lithium iron manganese phosphate/carbon composites via sol-gel process accompanied by phase separation

Macroporous lithium manganese iron phosphate/carbon (LiFe0.9Mn0.1PO4/C) has been successfully synthesized via a sol-gel process accompanied by phase separation. Poly (ethylene oxide) (PEO) acts as a phase separation inducer, while polyvinylpyrrolidone (PVP) synergistically regulates the morphology of the gel skeleton and serves as a reducing agent. Propylene oxide (PO) works as a proton scavenger to initiate the homogeneous gelation and modify the macrostructure. An appropriate amount of PEO, PVP and PO led to the formation of xerogel monoliths characterized by a three-dimensional co-continuous skeleton and interconnected macropores. The amorphous xerogel upon heat treatment at 400 °C for 2 h under a N2 atmosphere, formed carbon-coated LiFe0.9Mn0.1PO4/C crystals with excellent crystallinity and uniform elemental distribution. The resultant macroporous LFMP/C has a discharge capacity of 113.43 mA h g− 1 at 0.1 C, with a first coulombic efficiency of 90.1% and excellent capacity recovery rate after high-rate tests.

求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Journal of Porous Materials
Journal of Porous Materials 工程技术-材料科学:综合
CiteScore
4.80
自引率
7.70%
发文量
203
审稿时长
2.6 months
期刊介绍: The Journal of Porous Materials is an interdisciplinary and international periodical devoted to all types of porous materials. Its aim is the rapid publication of high quality, peer-reviewed papers focused on the synthesis, processing, characterization and property evaluation of all porous materials. The objective is to establish a unique journal that will serve as a principal means of communication for the growing interdisciplinary field of porous materials. Porous materials include microporous materials with 50 nm pores. Examples of microporous materials are natural and synthetic molecular sieves, cationic and anionic clays, pillared clays, tobermorites, pillared Zr and Ti phosphates, spherosilicates, carbons, porous polymers, xerogels, etc. Mesoporous materials include synthetic molecular sieves, xerogels, aerogels, glasses, glass ceramics, porous polymers, etc.; while macroporous materials include ceramics, glass ceramics, porous polymers, aerogels, cement, etc. The porous materials can be crystalline, semicrystalline or noncrystalline, or combinations thereof. They can also be either organic, inorganic, or their composites. The overall objective of the journal is the establishment of one main forum covering the basic and applied aspects of all porous materials.
期刊最新文献
Correction: One-step synthesis of CuO/MCM-41 nanocomposites and their application in photocatalytic degradation of dyes Modification of SBA-15 for stabilizing supported oxides Lotus leaf-derived capacitive carbon for zinc-ion hybrid supercapacitors prepared by one-step molten salt carbonization Influence of various templates on the performance of MFI zeolite in catalytic synthesis of trioxane Facile synthesis of copper sulfide loaded mesoporous organosilica nanospheres with a triple-shelled hollow structure
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1