Nikolai Khokhlov, Ivan Grishchenko, Ekaterina Shevelkina, Denis Bindyug, Ekaterina Barkanova, Dmitry Denisov, Dmitry Demushkin, Ivan Telegin, Ekaterina Yezhikova, Igor Avetissov, Roman Avetisov, Alexey Konyashkin, Oleg Ryabushkin
{"title":"高光学质量 LiNa5Mo9O30 晶体的晶体生长","authors":"Nikolai Khokhlov, Ivan Grishchenko, Ekaterina Shevelkina, Denis Bindyug, Ekaterina Barkanova, Dmitry Denisov, Dmitry Demushkin, Ivan Telegin, Ekaterina Yezhikova, Igor Avetissov, Roman Avetisov, Alexey Konyashkin, Oleg Ryabushkin","doi":"10.3390/cryst14090792","DOIUrl":null,"url":null,"abstract":"The bulk of the LiNa5Mo9O30 (LNM) crystals were successfully grown in the [010] and [001] directions without internal inclusions and cracks, using the Czochralski method with a low temperature gradient. The crystal grown in the [010] direction showed a tendency to twinning. The crystal grown in the [001] direction demonstrated high structural perfection (FWHM = 13″) for the (001) plane and high optical quality Δn ≈ 2 × 10−5. The laser-induced damage threshold was measured along a, b and c axes and was 12.2, 27.0 and 27.5 J/cm2, respectively. The thermo-optical coefficient dn/dT was measured for the main crystallographic axes, which was −5.75 × 10−6, −20.2 × 10−6 and 3.65 × 10−6 K−1 along the a, b and c axes, respectively. The second harmonic generation (SHG) was conducted in the crystalline LNM sample. The maximum efficiency value of 3.5% at a pump power of 12 W was achieved.","PeriodicalId":10855,"journal":{"name":"Crystals","volume":"58 1","pages":""},"PeriodicalIF":2.4000,"publicationDate":"2024-09-07","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Crystal Growth of LiNa5Mo9O30 Crystals of High Optical Quality\",\"authors\":\"Nikolai Khokhlov, Ivan Grishchenko, Ekaterina Shevelkina, Denis Bindyug, Ekaterina Barkanova, Dmitry Denisov, Dmitry Demushkin, Ivan Telegin, Ekaterina Yezhikova, Igor Avetissov, Roman Avetisov, Alexey Konyashkin, Oleg Ryabushkin\",\"doi\":\"10.3390/cryst14090792\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The bulk of the LiNa5Mo9O30 (LNM) crystals were successfully grown in the [010] and [001] directions without internal inclusions and cracks, using the Czochralski method with a low temperature gradient. The crystal grown in the [010] direction showed a tendency to twinning. The crystal grown in the [001] direction demonstrated high structural perfection (FWHM = 13″) for the (001) plane and high optical quality Δn ≈ 2 × 10−5. The laser-induced damage threshold was measured along a, b and c axes and was 12.2, 27.0 and 27.5 J/cm2, respectively. The thermo-optical coefficient dn/dT was measured for the main crystallographic axes, which was −5.75 × 10−6, −20.2 × 10−6 and 3.65 × 10−6 K−1 along the a, b and c axes, respectively. The second harmonic generation (SHG) was conducted in the crystalline LNM sample. The maximum efficiency value of 3.5% at a pump power of 12 W was achieved.\",\"PeriodicalId\":10855,\"journal\":{\"name\":\"Crystals\",\"volume\":\"58 1\",\"pages\":\"\"},\"PeriodicalIF\":2.4000,\"publicationDate\":\"2024-09-07\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Crystals\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.3390/cryst14090792\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"CRYSTALLOGRAPHY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Crystals","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.3390/cryst14090792","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"CRYSTALLOGRAPHY","Score":null,"Total":0}
Crystal Growth of LiNa5Mo9O30 Crystals of High Optical Quality
The bulk of the LiNa5Mo9O30 (LNM) crystals were successfully grown in the [010] and [001] directions without internal inclusions and cracks, using the Czochralski method with a low temperature gradient. The crystal grown in the [010] direction showed a tendency to twinning. The crystal grown in the [001] direction demonstrated high structural perfection (FWHM = 13″) for the (001) plane and high optical quality Δn ≈ 2 × 10−5. The laser-induced damage threshold was measured along a, b and c axes and was 12.2, 27.0 and 27.5 J/cm2, respectively. The thermo-optical coefficient dn/dT was measured for the main crystallographic axes, which was −5.75 × 10−6, −20.2 × 10−6 and 3.65 × 10−6 K−1 along the a, b and c axes, respectively. The second harmonic generation (SHG) was conducted in the crystalline LNM sample. The maximum efficiency value of 3.5% at a pump power of 12 W was achieved.
期刊介绍:
Crystals (ISSN 2073-4352) is an open access journal that covers all aspects of crystalline material research. Crystals can act as a reference, and as a publication resource, to the community. It publishes reviews, regular research articles, and short communications. Our aim is to encourage scientists to publish their experimental and theoretical results in as much detail as possible. Therefore, there is no restriction on article length. Full experimental details must be provided to enable the results to be reproduced. Crystals provides a forum for the advancement of our understanding of the nucleation, growth, processing, and characterization of crystalline materials. Their mechanical, chemical, electronic, magnetic, and optical properties, and their diverse applications, are all considered to be of importance.