F. F. Malyavin, V. E. Suprunchuk, V. A. Tarala, A. A. Kravtsov, D. S. Vakalov, V. A. Lapin, K. V. Kungurtsev, E. V. Medyanik, L. V. Tarala
{"title":"基于钇铝石榴石的陶瓷/单晶复合材料的制造与特性","authors":"F. F. Malyavin, V. E. Suprunchuk, V. A. Tarala, A. A. Kravtsov, D. S. Vakalov, V. A. Lapin, K. V. Kungurtsev, E. V. Medyanik, L. V. Tarala","doi":"10.1007/s10717-024-00688-9","DOIUrl":null,"url":null,"abstract":"<p>The optical properties and microstructure of composites based on yttrium aluminum garnet were studied. The composites were produced by vacuum sintering of pre-formed compacts of nanocrystalline powder (Y<sub>3</sub>Al<sub>4.995</sub>Cr<sub>0.005</sub>O<sub>12</sub>) with a YAG single crystal. The transmittance spectra of the composite samples exhibited the presence of Cr<sup>3+</sup> absorption bands following vacuum sintering, as well as Cr<sup>4+</sup> bands following annealing in air. The impact of varying heating rates during vacuum sintering on the transmittance of composite samples was examined. It was determined that the optimal heating rate during the vacuum sintering of composites should be less or equal to 120 K/h. In addition, the impact of the vacuum sintering temperature on the optical properties and microstructure of YAG:Cr (ceramics)/YAG:Nd (single crystal) composite samples was investigated. The samples exhibiting the highest transparency were obtained at a temperature of 1850°C. Microstructure studies of the composites revealed the presence of regular residual porosity in the vicinity of the interface, predominantly located in the YAG single crystal. It is postulated that the formation of these pores occurs during the fusion of ceramic grains with a single crystal during sintering.</p>","PeriodicalId":579,"journal":{"name":"Glass and Ceramics","volume":"81 5-6","pages":"230 - 236"},"PeriodicalIF":0.6000,"publicationDate":"2024-10-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Fabrication and Properties of Ceramics/Single Crystal Composites Based on Yttrium Aluminum Garnet\",\"authors\":\"F. F. Malyavin, V. E. Suprunchuk, V. A. Tarala, A. A. Kravtsov, D. S. Vakalov, V. A. Lapin, K. V. Kungurtsev, E. V. Medyanik, L. V. Tarala\",\"doi\":\"10.1007/s10717-024-00688-9\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p>The optical properties and microstructure of composites based on yttrium aluminum garnet were studied. The composites were produced by vacuum sintering of pre-formed compacts of nanocrystalline powder (Y<sub>3</sub>Al<sub>4.995</sub>Cr<sub>0.005</sub>O<sub>12</sub>) with a YAG single crystal. The transmittance spectra of the composite samples exhibited the presence of Cr<sup>3+</sup> absorption bands following vacuum sintering, as well as Cr<sup>4+</sup> bands following annealing in air. The impact of varying heating rates during vacuum sintering on the transmittance of composite samples was examined. It was determined that the optimal heating rate during the vacuum sintering of composites should be less or equal to 120 K/h. In addition, the impact of the vacuum sintering temperature on the optical properties and microstructure of YAG:Cr (ceramics)/YAG:Nd (single crystal) composite samples was investigated. The samples exhibiting the highest transparency were obtained at a temperature of 1850°C. Microstructure studies of the composites revealed the presence of regular residual porosity in the vicinity of the interface, predominantly located in the YAG single crystal. It is postulated that the formation of these pores occurs during the fusion of ceramic grains with a single crystal during sintering.</p>\",\"PeriodicalId\":579,\"journal\":{\"name\":\"Glass and Ceramics\",\"volume\":\"81 5-6\",\"pages\":\"230 - 236\"},\"PeriodicalIF\":0.6000,\"publicationDate\":\"2024-10-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Glass and Ceramics\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://link.springer.com/article/10.1007/s10717-024-00688-9\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MATERIALS SCIENCE, CERAMICS\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Glass and Ceramics","FirstCategoryId":"88","ListUrlMain":"https://link.springer.com/article/10.1007/s10717-024-00688-9","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, CERAMICS","Score":null,"Total":0}
Fabrication and Properties of Ceramics/Single Crystal Composites Based on Yttrium Aluminum Garnet
The optical properties and microstructure of composites based on yttrium aluminum garnet were studied. The composites were produced by vacuum sintering of pre-formed compacts of nanocrystalline powder (Y3Al4.995Cr0.005O12) with a YAG single crystal. The transmittance spectra of the composite samples exhibited the presence of Cr3+ absorption bands following vacuum sintering, as well as Cr4+ bands following annealing in air. The impact of varying heating rates during vacuum sintering on the transmittance of composite samples was examined. It was determined that the optimal heating rate during the vacuum sintering of composites should be less or equal to 120 K/h. In addition, the impact of the vacuum sintering temperature on the optical properties and microstructure of YAG:Cr (ceramics)/YAG:Nd (single crystal) composite samples was investigated. The samples exhibiting the highest transparency were obtained at a temperature of 1850°C. Microstructure studies of the composites revealed the presence of regular residual porosity in the vicinity of the interface, predominantly located in the YAG single crystal. It is postulated that the formation of these pores occurs during the fusion of ceramic grains with a single crystal during sintering.
期刊介绍：
Glass and Ceramics reports on advances in basic and applied research and plant production techniques in glass and ceramics. The journal''s broad coverage includes developments in the areas of silicate chemistry, mineralogy and metallurgy, crystal chemistry, solid state reactions, raw materials, phase equilibria, reaction kinetics, physicochemical analysis, physics of dielectrics, and refractories, among others.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们