Enhancing bending strength in continuous drive friction welding of PEEK polymer cylinders through the innovative progressively increased welding area method

The continuous drive friction welding (CDFW) stands out for its low energy consumption within the welding realm. Polyetheretherketone (PEEK) represents a high-performance engineering thermoplastic, falling under the polyaryletherketone family. Renowned for its outstanding mechanical, thermal, and chemical attributes, PEEK finds utility across a diverse array of industries. However, the discovery of numerous voids at the weld interface has revealed limitations in the mechanical properties of PEEK welded samples. This study introduces an innovative approach named progressively increased welding area (PIWA) method, to mitigate voids within the weld interface. In general, the Taguchi method was used to optimize the process parameters of CDFW of dissimilar PEEK round rods to reduce random efforts by the trial-and-error method. It was found that the proposed PIWA method can definitely enhance the bending strength of rotational friction welded samples due to reduction of voids inside the weld interface. The optimal process parameters for the CDFW with the PIWA method involve a rotational speed of 2500 rpm, a cone angle of 120°, a cone top width of 8 mm, and a feed rate of 0.1 mm/s. The most influential factor affecting the bending strength of the PEEK welded samples is the feed rate, followed by cone angle, rotational speed, and cone top width. Specifically, the contribution ratios for feed rate, cone angle, rotational speed, and cone top width are about 71 %, 20 %, 7 %, and 2 %, respectively. The confirmation tests showed that the bending strength of the PEEK welded samples using optimal process parameters can be increased by approximately 68 % compared with the maximum bending strength of 180 MPa using the conventional method with a cone angle of 180° The proposed PIWA method has industrial applicability and practical value because this technique can enhance the mechanical properties of PEEK welded samples under low environmental pollution and energy consumption.