{"title":"架空导体加热室和温度对铝合金 6201-T81 导体疲劳寿命的影响","authors":"Ricardo Lenon Da Silva Rodrigues, Miguel Angel Garcia, José Alexander Araújo, Jorge Luiz De Almeida Ferreira, Cosme Roberto Moreira da Silva, Remy Kalombo Badibanga","doi":"10.1111/ffe.14421","DOIUrl":null,"url":null,"abstract":"<p>This work investigates the impact of temperature on the fatigue life All Aluminum Alloy Conductors (AAAC) made of 6201-T81. A heating chamber was developed to simulate thermal effects induced by electric current passage. Wöhler fatigue curves were generated under isothermal conditions at 75 and 150°C and later compared with the one at 20°C. The conductor exhibited similar fatigue life at 20 and 75°C; however, a significant increase of life was observed for tests at 150°C. Hardness tests and failure analysis of wire breakages were carried out on samples extracted from the conductor coil and on artificially aged samples maintained at controlled temperatures. The analyses revealed that at a temperature of 150°C, there is formation of small precipitates of magnesium and silicon within the aluminum matrix, which impeded the propagation of discontinuities, increasing the material's hardness and fatigue resistance.</p>","PeriodicalId":12298,"journal":{"name":"Fatigue & Fracture of Engineering Materials & Structures","volume":"47 11","pages":"4151-4164"},"PeriodicalIF":3.1000,"publicationDate":"2024-08-21","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Overhead conductor heating chamber and temperature effects on the fatigue life of aluminum alloy 6201-T81 conductors\",\"authors\":\"Ricardo Lenon Da Silva Rodrigues, Miguel Angel Garcia, José Alexander Araújo, Jorge Luiz De Almeida Ferreira, Cosme Roberto Moreira da Silva, Remy Kalombo Badibanga\",\"doi\":\"10.1111/ffe.14421\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p>This work investigates the impact of temperature on the fatigue life All Aluminum Alloy Conductors (AAAC) made of 6201-T81. A heating chamber was developed to simulate thermal effects induced by electric current passage. Wöhler fatigue curves were generated under isothermal conditions at 75 and 150°C and later compared with the one at 20°C. The conductor exhibited similar fatigue life at 20 and 75°C; however, a significant increase of life was observed for tests at 150°C. Hardness tests and failure analysis of wire breakages were carried out on samples extracted from the conductor coil and on artificially aged samples maintained at controlled temperatures. The analyses revealed that at a temperature of 150°C, there is formation of small precipitates of magnesium and silicon within the aluminum matrix, which impeded the propagation of discontinuities, increasing the material's hardness and fatigue resistance.</p>\",\"PeriodicalId\":12298,\"journal\":{\"name\":\"Fatigue & Fracture of Engineering Materials & Structures\",\"volume\":\"47 11\",\"pages\":\"4151-4164\"},\"PeriodicalIF\":3.1000,\"publicationDate\":\"2024-08-21\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Fatigue & Fracture of Engineering Materials & Structures\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://onlinelibrary.wiley.com/doi/10.1111/ffe.14421\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"ENGINEERING, MECHANICAL\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Fatigue & Fracture of Engineering Materials & Structures","FirstCategoryId":"88","ListUrlMain":"https://onlinelibrary.wiley.com/doi/10.1111/ffe.14421","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"ENGINEERING, MECHANICAL","Score":null,"Total":0}
Overhead conductor heating chamber and temperature effects on the fatigue life of aluminum alloy 6201-T81 conductors
This work investigates the impact of temperature on the fatigue life All Aluminum Alloy Conductors (AAAC) made of 6201-T81. A heating chamber was developed to simulate thermal effects induced by electric current passage. Wöhler fatigue curves were generated under isothermal conditions at 75 and 150°C and later compared with the one at 20°C. The conductor exhibited similar fatigue life at 20 and 75°C; however, a significant increase of life was observed for tests at 150°C. Hardness tests and failure analysis of wire breakages were carried out on samples extracted from the conductor coil and on artificially aged samples maintained at controlled temperatures. The analyses revealed that at a temperature of 150°C, there is formation of small precipitates of magnesium and silicon within the aluminum matrix, which impeded the propagation of discontinuities, increasing the material's hardness and fatigue resistance.
期刊介绍：
Fatigue & Fracture of Engineering Materials & Structures (FFEMS) encompasses the broad topic of structural integrity which is founded on the mechanics of fatigue and fracture, and is concerned with the reliability and effectiveness of various materials and structural components of any scale or geometry. The editors publish original contributions that will stimulate the intellectual innovation that generates elegant, effective and economic engineering designs. The journal is interdisciplinary and includes papers from scientists and engineers in the fields of materials science, mechanics, physics, chemistry, etc.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们