Hydrodynamic Flexible Spindle (HydroFlex) Polishing of turbine blade internal cooling channels for oxide removal

Internal cooling channels are essential to turbine blades for high efficiency power generation. Effective removal of aluminum oxide build-up in turbine blade cooling channels is of critical importance to refurbishment and prolonged service life of turbine blades. Conventional internal polishing processes, including abrasive flow machining, chemical polishing, and electrical discharge machining cannot effectively remove the oxide layer within the internal cooling channels due to the complex geometry with high aspect ratio and diameter variation and the electric insulation of the oxide layer. In this case study, we investigated the application of a novel hydrodynamic flexible-spindle (HydroFlex) polishing process to remove the oxide layer within the internal cooling channels of an Inconel 738 turbine blade that was taken out of serve due to oxide build-up. For a 350 mm long cooling channel featured with an inner diameter transition from ϕ4 mm to ϕ2.5 mm, within 12 min, at the grinding wheel rotational speed of 50,000 rpm and 30,000 rpm, HydroFlex was able to completely remove the 14.31 µm thick oxide layer off from the wall of the turbine blade internal cooling channel, improve the channel circularity by 54.7 %, and decrease the channel surface roughness by up to 64.3 %. The results demonstrated the effectiveness of HydroFlex in polishing complex internal cooling channels of turbine blades for oxide removal and potential blade service life extension.