Corrigendum to “Enhancement on mechanical properties via phase separation induced by Cu-added high-entropy alloy fillers in metastable ferrous medium-entropy alloy welds” [J. Alloy. Compd. 1010 (2025) 177321]

The author regrets the following:

• 1)I would like to replace the Fig. 2 with the following figure as there is a typo in the original Fig. 2.

  

  1. Download: Download high-res image (520KB)
  2. Download: Download full-size image

  Fig. 2. Weldability and compositional behaviour in GTA welds using CoFeMnNiCu and (CoFeMnNi)₇₀Cu₃₀ fillers: (a) Macroscopical views of the BSE image and (b) compositional behaviours of the cross-sections in transverse GTA welds. Yellow and red dashed lines indicate the fusion line and the location of quantitative EPMA, respectively.

• 2)There is a blank space after = in Eqs. (2) and (4). The corrected equations are follows:

(2)$\delta =100\sqrt{\sum _{i=1}^n{C}_i{\left(1-\frac{r_i}{\overline{r}}\right)}^2},\overline{r}=\sum _{i=1}^n{C}_i{r}_i$$\delta =100\sqrt{\sum _{i=1}^n{C}_i{\left(1-\frac{r_i}{\overline{r}}\right)}^2},\overline{r}=\sum _{i=1}^n{C}_i{r}_i$(4)${\rho }_{111}=\frac{4}{\sqrt{3}}\frac{1}{a^2{N}_A}$${\rho }_{111}=\frac{4}{\sqrt{3}}\frac{1}{a^2{N}_A}$