Changes in physical-mechanical properties and chemical compositions of Toona sinensis wood before and after thermal treatment.

Vacuum heat treatment was used to improve the dimensional stability of Toona sinensis wood in this study, the shrinking and swelling rates, the physical-mechanical properties, and the chemical compositions before and after the thermal treatment were evaluated. The results revealed that the volume shrinkage and swelling rate for the heat-treated wood samples were decreased by 45.60% and 49.95%, respectively at 220°C for 6 h indicating that thermal treatment could obviously improve the dimensional stability of Toona sinensis wood. Thermal treatment also decreased the mechanical strength. The surface color was changed by the treatment. The chemical composition results showed the decrease in density and mechanical strength was due to the partial degradation of hemicellulose during the treatment. The results of this study that vacuum heat treatment could improve the dimensional stability by sacrificing somewhat mechanical strength, the treatment conditions mainly the temperature should be properly controlled to archive an optimized improvement in dimensional stability with minimum reduction in mechanical strength.