Effects of heat treatment on the behavior of teak wood adherends bonded joints

The main aim of this work is to investigate the effect of heat treatment on the teak wood adherend bonded joints. Indian teak wood samples were kept in an oven at 150?°C for 2?h for the heat treatment process. The surface roughness values of the wood adherend before and after the heat treatment process were measured using a surface profilometer. Wettability of un-treated and heat-treated teak wood samples was determined with the contact angle measurements by using the sessile drop method. Single strap joints with un-treated and heat treated wood specimens were tested at ambient temperature. The results show that, there is a clear dependency observed in between the heat treatment and the surface roughness of the wood adherends. Wettability of teak wood adherend surface is degraded after the heat treatment process. An adverse effect of heat treatment of wood adherend on the bonding strength was observed, but the surface roughness was improved.