{"title":"改善烧结致密性和性能的富铝铝酸钙耐火材料的制备","authors":"Tianpeng Wen, Yao Jin, Zhaoyang Liu, Zhengguo Yan, Jingkun Yu, Lei Yuan","doi":"10.1007/s41779-023-00849-z","DOIUrl":null,"url":null,"abstract":"<div><h2>Abstract\n</h2><div><p>\nThe present work focused on the evolution characteristics in the microstructure and properties of calcium aluminate composite ceramics after heat treatment for raw materials at different temperatures. The results showed that the apparent porosity of all the sintered samples firstly decreased to the minimum at a heat treatment temperature of 1200 °C and then increased with increasing heat treatment temperature. The compressive strength was greatly enhanced after the heat treatment for raw materials due to the significant decrease in porosity, presenting the opposite relationship with the change of porosity. The formation of the interlaced structure in the sintered samples was conducive to improving the densification of the calcium aluminate ceramics. This work provided new avenues of thought regarding the manufacturing of calcium aluminate ceramics and promoted its better application in metallurgy.</p></div></div>","PeriodicalId":49042,"journal":{"name":"Journal of the Australian Ceramic Society","volume":"59 3","pages":"545 - 554"},"PeriodicalIF":1.9000,"publicationDate":"2023-03-14","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Preparation of alumina-rich calcium aluminate refractories with improved sintering densification and properties\",\"authors\":\"Tianpeng Wen, Yao Jin, Zhaoyang Liu, Zhengguo Yan, Jingkun Yu, Lei Yuan\",\"doi\":\"10.1007/s41779-023-00849-z\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><h2>Abstract\\n</h2><div><p>\\nThe present work focused on the evolution characteristics in the microstructure and properties of calcium aluminate composite ceramics after heat treatment for raw materials at different temperatures. The results showed that the apparent porosity of all the sintered samples firstly decreased to the minimum at a heat treatment temperature of 1200 °C and then increased with increasing heat treatment temperature. The compressive strength was greatly enhanced after the heat treatment for raw materials due to the significant decrease in porosity, presenting the opposite relationship with the change of porosity. The formation of the interlaced structure in the sintered samples was conducive to improving the densification of the calcium aluminate ceramics. This work provided new avenues of thought regarding the manufacturing of calcium aluminate ceramics and promoted its better application in metallurgy.</p></div></div>\",\"PeriodicalId\":49042,\"journal\":{\"name\":\"Journal of the Australian Ceramic Society\",\"volume\":\"59 3\",\"pages\":\"545 - 554\"},\"PeriodicalIF\":1.9000,\"publicationDate\":\"2023-03-14\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of the Australian Ceramic Society\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://link.springer.com/article/10.1007/s41779-023-00849-z\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q3\",\"JCRName\":\"Materials Science\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of the Australian Ceramic Society","FirstCategoryId":"88","ListUrlMain":"https://link.springer.com/article/10.1007/s41779-023-00849-z","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"Materials Science","Score":null,"Total":0}
Preparation of alumina-rich calcium aluminate refractories with improved sintering densification and properties
Abstract
The present work focused on the evolution characteristics in the microstructure and properties of calcium aluminate composite ceramics after heat treatment for raw materials at different temperatures. The results showed that the apparent porosity of all the sintered samples firstly decreased to the minimum at a heat treatment temperature of 1200 °C and then increased with increasing heat treatment temperature. The compressive strength was greatly enhanced after the heat treatment for raw materials due to the significant decrease in porosity, presenting the opposite relationship with the change of porosity. The formation of the interlaced structure in the sintered samples was conducive to improving the densification of the calcium aluminate ceramics. This work provided new avenues of thought regarding the manufacturing of calcium aluminate ceramics and promoted its better application in metallurgy.
期刊介绍：
Publishes high quality research and technical papers in all areas of ceramic and related materials
Spans the broad and growing fields of ceramic technology, material science and bioceramics
Chronicles new advances in ceramic materials, manufacturing processes and applications
Journal of the Australian Ceramic Society since 1965
Professional language editing service is available through our affiliates Nature Research Editing Service and American Journal Experts at the author''s cost and does not guarantee that the manuscript will be reviewed or accepted
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们