THE POTENTIAL OF PRODUCING HIGH ADDED VALUE STRUCTURAL TIMBER FROM LAMELLAE WASTE. CLASSIFICATION AND VISUAL GRADING

This study is the continuation of the first part (Horváth et al. 2023), in which density, bending strength and modulus of elasticity of 100 oak lamellae generated as small-sized production waste were investigated. In this part of the study series, the classification of our sample set is carried out according to the EN 338. A visual pre-grading is presented, to remove the worst specimens and achieve a better final result and a standardized visual grading is also shown. Our results are compared with literature values of clear specimens as well. Amount of 80% of the specimens were found to be suitable for further structural use. The total sample set is classified in strength class D35 (average density 712.6±72.5 kg/m3; average MoRadj 65.4±16.2 MPa; average MoEadj 13.4±3.1 GPa), while the visually pre-graded part with better average test results is classified in strength class D45. Industrial wood residues contain a sufficiently high proportion of elements for further processing, so that after sorting it can be used as raw material for glued-laminated load-bearing timber.