闪光对接焊优质钢轨残余应力的x射线衍射分析

IF 0.3 4区 材料科学 Q4 METALLURGY & METALLURGICAL ENGINEERING Soldagem & Inspecao Pub Date : 2020-01-01 DOI:10.1590/0104-9224/si25.29
Bras Senra de Oliveira, Lino Alberto Soares Rodrigues, E. S. Costa, E. Braga, M. Reis
{"title":"闪光对接焊优质钢轨残余应力的x射线衍射分析","authors":"Bras Senra de Oliveira, Lino Alberto Soares Rodrigues, E. S. Costa, E. Braga, M. Reis","doi":"10.1590/0104-9224/si25.29","DOIUrl":null,"url":null,"abstract":"Abstract: This work is distinguished by searching for a non-destructive technology, and X-ray diffraction was validated by the XStress 3000 analyser. Measurements of residual stresses in the welded zone of premium pearlitic rails was performed, rail surface hardness of 370 HB and 0.79% carbon content. The welding of the rails was done by flash butt process, performed by Schlatter GAAS 80 stationary equipment. The results of the tensile and compressive stress measurements identified the residual stresses in the welded zone, with specific zones of tensile stresses misplaced at the weld center, with values up to 391 MPa, and compressive stresses, with values up to -166 MPa, as it moves away rails weld center. An important point of this study is the residual stress measurement considering a complete welding process, including: pre-grinding, flash butt welding, heat treatment, finishing grinding and straightening. Lastly, was observed the welding technique potentially can induce residual stresses at rails.","PeriodicalId":49500,"journal":{"name":"Soldagem & Inspecao","volume":"1 1","pages":""},"PeriodicalIF":0.3000,"publicationDate":"2020-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"2","resultStr":"{\"title\":\"X-Ray Diffraction Analysis of Residual Stresses in the Premium Rails Welded by Flash Butt Process\",\"authors\":\"Bras Senra de Oliveira, Lino Alberto Soares Rodrigues, E. S. Costa, E. Braga, M. Reis\",\"doi\":\"10.1590/0104-9224/si25.29\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Abstract: This work is distinguished by searching for a non-destructive technology, and X-ray diffraction was validated by the XStress 3000 analyser. Measurements of residual stresses in the welded zone of premium pearlitic rails was performed, rail surface hardness of 370 HB and 0.79% carbon content. The welding of the rails was done by flash butt process, performed by Schlatter GAAS 80 stationary equipment. The results of the tensile and compressive stress measurements identified the residual stresses in the welded zone, with specific zones of tensile stresses misplaced at the weld center, with values up to 391 MPa, and compressive stresses, with values up to -166 MPa, as it moves away rails weld center. An important point of this study is the residual stress measurement considering a complete welding process, including: pre-grinding, flash butt welding, heat treatment, finishing grinding and straightening. Lastly, was observed the welding technique potentially can induce residual stresses at rails.\",\"PeriodicalId\":49500,\"journal\":{\"name\":\"Soldagem & Inspecao\",\"volume\":\"1 1\",\"pages\":\"\"},\"PeriodicalIF\":0.3000,\"publicationDate\":\"2020-01-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"2\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Soldagem & Inspecao\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1590/0104-9224/si25.29\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"METALLURGY & METALLURGICAL ENGINEERING\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Soldagem & Inspecao","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1590/0104-9224/si25.29","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 2

摘要

摘要:本工作通过寻找一种无损技术来区分,并通过XStress 3000分析仪对x射线衍射进行了验证。对优质珠光体钢轨焊接区残余应力进行了测量,钢轨表面硬度为370 HB,含碳量为0.79%。钢轨的焊接采用闪光对接工艺,采用schlater GAAS 80固定式设备进行焊接。拉伸和压应力测量的结果确定了焊接区域的残余应力,在焊缝中心的特定区域,拉伸应力的值高达391 MPa,压应力的值高达-166 MPa,因为它远离轨道焊接中心。本研究的一个重点是残余应力的测量,考虑了一个完整的焊接过程,包括:预磨、闪光对焊、热处理、精磨和矫直。最后,分析了焊接工艺对钢轨残余应力的潜在影响。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
X-Ray Diffraction Analysis of Residual Stresses in the Premium Rails Welded by Flash Butt Process
Abstract: This work is distinguished by searching for a non-destructive technology, and X-ray diffraction was validated by the XStress 3000 analyser. Measurements of residual stresses in the welded zone of premium pearlitic rails was performed, rail surface hardness of 370 HB and 0.79% carbon content. The welding of the rails was done by flash butt process, performed by Schlatter GAAS 80 stationary equipment. The results of the tensile and compressive stress measurements identified the residual stresses in the welded zone, with specific zones of tensile stresses misplaced at the weld center, with values up to 391 MPa, and compressive stresses, with values up to -166 MPa, as it moves away rails weld center. An important point of this study is the residual stress measurement considering a complete welding process, including: pre-grinding, flash butt welding, heat treatment, finishing grinding and straightening. Lastly, was observed the welding technique potentially can induce residual stresses at rails.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Soldagem & Inspecao
Soldagem & Inspecao 工程技术-冶金工程
CiteScore
1.00
自引率
16.70%
发文量
13
审稿时长
12 weeks
期刊介绍: The Journal Soldagem & Inspeção (S&I) js a techno-scientific journal created in 1995. Printed issues of this journal are distributed free of charge to libraries in Brazil, Latin America and the Iberian Peninsula. It has been printed regularly every quarter since September, 2002, and, since the beginning of 2007, its electronic version is available in the address: (http://www.abs-soldagem.org.br/s&i/). The journal is sponsored by the Brazilian Welding Association (ABS). Since its creation several well known professionals working in welding contributed with the Journal Soldagem & Inspeção and its editorial board crosses the Brazilian borders. During its evolution the Journal received ta special contribution from the Editors-in-chief : Ronaldo Paranhos, Américo Scoti, Paulo Modenesi e Alexandre Bracarence. Since January 2012 the Editor-in-chief is Ana Sofia C. M. D’Oliveira, Full professor at Universidade Federal do Paraná (UFPR) . Her work focus mainly on Hardfacing and Physical Metallurgy. The jornal Soldagem & Inspeção also counts with 10 Associate Editors and a fix Editorial board of referees. short-term (Ad Hoc) referees can be invited to evaluate some papers submitted to the journal. The Soldagem & Inspeção journal is the scientific divulgation channel of the Brazilian Welding Association (ABS). It aims to publish original papers related to the scientific and technological development of welding, inspection, and related fields. Review papers or letters on current and controversial subjects are also published in the Journal. Its abbreviated title is Soldag. insp. (Impr.), which should be used in bibliographies, footnotes and bibliographical references and strips.
期刊最新文献
Conjuntos Soldados Submetidos a Carregamento Excêntrico Quase Estático e de Impacto Estrutural “Fora do Plano” Evaluation of the Effect of Heat Input and Cooling Rate of Rail Flash-Butt Welding using Finite Element Method Simulation Influencia de la Atmosfera de N2 en los Parámetros Operacionales y la Microestructura del Depósito en el Recargue Duro con FCAW Simulações Computacionais dos Processos de Manufatura Aditiva de Metais: Um Review Introdutório Evolução dos Processos de Automação em Células de Soldagem: Uma Revisão da Literatura
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1