Effect of Post-Curing Time on the Color Stability and Related Properties of a Tooth-Colored 3D-Printed Resin Material

This study investigated the effect of post-curing time on the color stability and related properties, such as degree of conversion (DC), surface roughness, water contact angle, water sorption (Wsp), and water solubility (Wsl) of 3D-printed resin for dental restorations. The 3D-printed specimens were divided into four groups according to the post-curing time (0, 5, 10, and 20 min). Color changes (ΔE00) of the specimens immersed in aging media were measured using a spectrophotometer at different aging times. The DC of the resin was measured using a FTIR. The surface roughness (Ra) of the resin immersed in coffee was measured at different aging times. Water contact angle was evaluated using the sessile drop method, and Wsp and Wsl were tested according to the ISO 4049:2019. The ΔE00 values of the specimens immersed in coffee and red wine decreased with increasing post-curing time. As the post-curing time increased up to 10 min, the DC increased and water contact angle decreased. The Ra value of the group without post-curing (0 min) increased gradually for 30 days, except between 7 and 15 days. However, when the post-curing time increased to greater than 10 min, no apparent change in Ra value was detected. The Wsp and Wsl of the group without post-curing were significantly lower and larger than that of the other groups, respectively. The longer the post-curing time of the tooth-colored 3D-printed resin, the better the color stability. The post-curing time of the 3D-printed resin affected the DC, surface roughness after aging in the staining media, water contact angle, water sorption, and water solubility.