Burnability and Mineral Properties of Clinker Added Chlorine

In this study, raw mix was mixed with CaCl2 for analyzing characteristics of clinker added chlorine and chlorine was added by 2,000ppm at high concentration condition. The raw mix added chlorine was burned at 1250°C~1350°C and maintained during 10minutes at each maximum temperature. Clinker target modulus was LSF 92, SM 2.5 and IM 1.6 in this study. The burnability of clinker added chlorine was identified by free-CaO content. Free-CaO content decreased as chlorine content increased and free-CaO content of 1350°C-2000ppm clinker decreased by 1.5%. Optical microscope and XRD Analyses were used for identify mineral properties of clinker added chlorine. The mineral of clinker could not be observed at 1250°C and the size of alite grew larger as chlorine content increased at 1350°C. It showed a good crystallizability as chlorine content increased. As chlorine content of clinker increased, clinker showed a good burnability and mineral property.