Bacterial Community Analysis of Biofilm Formed on Metal Joint

Microbiologically influenced corrosion (MIC) is caused by biofilms formed on metal surfaces, and MIC of metal alloys on marine infrastructure leads to severe accidents and great economic losses. Although bacterial community analyses of the biofilms collected from corroded metal have been studied, the analyses of biofilms collected from uncorroded metal are rarely reported. In this study, a biofilm formed on an uncorroded metal joint attached to a metal dock mooring at Akitsu Port was used as a model for bacterial community analysis. The bacterial community was analyzed by high-throughput sequencing of the V3–V4 variable regions of the 16S rRNA gene. Bacterial species contained in the biofilms were identified at the genus level, and Alkanindiges bacteria were the dominant species, which have been not reported as the dominant species in previous research on MIC. The genome sequences of known Alkanindiges bacteria do not have conserved gene clusters required to cause metal corrosion, which suggests that Alkanindiges bacteria do not corrode metals but act on the formation of biofilms. Those findings indicated that the bacterial community may change significantly during the process from biofilm formation to the occurrence of metal corrosion.