Synthesis, Structural, and Optical Characterization of a New Europium(II) Tin Selenide, Eu8(Sn4Se14)(Se3)2 with a (Sn4Se14)12– Building Block

A new phase in europium-tin-chalcogenide chemistry has been prepared using the reactive flux method: Eu8(Sn4Se14)(Se3)2. The compound crystallizes in the orthorhombic space group P21212 with cell parameters a = 11.990(2) A, b = 16.425(4) A, c = 8.543(1) A, and Z = 2. Eu8(Sn4Se14)(Se3)2 is a three dimensional structure with EuII cations linked together with an unusual (Sn4Se14)12– anionic unit and (Se3)2– chains. UV-VIS-NIR band-gap analysis shows that these black metallic crystals are likely semiconductors with an optical band-gap of 1.07 eV. Synthese, Strukturen und optischen Eigenshaften einer neuen Europium(II)–Zinn–Selen-Phase – Eu8(Sn4Se12)(Se3)2 – mit einem ungewohnlichen (Sn4Se12)12–-Baustein Eine neue Phase in dem Europium/Zinn/Selen-System wurde mittels der Flusmittelmethode dargestellt. Eu8(Sn4Se12)(Se3)2 kistallisiert in der orthorhombische Raumgruppe P21212 mit 2 Formuleinheiten in der Elementarzelle. Die Ausgleichsrechnung ergab die Gitterkonstanten: a = 11.990(2) A, b = 16.425(4) A, c = 8.543(1) A. Eu8(Sn4Se12)(Se3)2 hat eine dreidimensional Struktur in der die EuII-Atome sowohl mit (Se3)2–-Ketten als auch mit dem ungewohnlichen Anion (Sn4Se12)12– verbunden sind. Bei polykristallinem Material ist die Messung der optische Bandlucke mittels der diffusen Reflexion eine geeignete Methode und lieferte 1.07 eV fur die hier beschriebene Phase.