{"title":"Glass-Ceramics Produced by Vitrification of Coal Fly Ash","authors":"B. Angjusheva, E. Fidančevska","doi":"10.7251/qol2103085a","DOIUrl":null,"url":null,"abstract":"Glass-ceramics based on CAS (CaO-Al2O3-SiO2) system was produced by controlled crystallization of vitrified fly ash. Fly ash was pre-treated by magnetic separation and nonmagnetic part of fly ash (NFA) was used. Maximal crystallization of parent glass occurs in the temperature region from 900 oC to 1160 oC. Glass-ceramics was produced by consolidation of parent glass i.e. pressing (45 MPa) and sintering at 950, 1000, 1050 and 1100 oC, and isothermal time at the final temperature of 30, 60, 120 minutes. The dominant crystalline phase was calcium aluminum silicate (anorthite). The obtained glass-ceramics could be potentially used in construction applications.","PeriodicalId":363723,"journal":{"name":"Quality of Life (Banja Luka) - APEIRON","volume":"13 4","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2021-10-03","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Quality of Life (Banja Luka) - APEIRON","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.7251/qol2103085a","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
Glass-ceramics based on CAS (CaO-Al2O3-SiO2) system was produced by controlled crystallization of vitrified fly ash. Fly ash was pre-treated by magnetic separation and nonmagnetic part of fly ash (NFA) was used. Maximal crystallization of parent glass occurs in the temperature region from 900 oC to 1160 oC. Glass-ceramics was produced by consolidation of parent glass i.e. pressing (45 MPa) and sintering at 950, 1000, 1050 and 1100 oC, and isothermal time at the final temperature of 30, 60, 120 minutes. The dominant crystalline phase was calcium aluminum silicate (anorthite). The obtained glass-ceramics could be potentially used in construction applications.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们