C. La-mei, Guangxun Liu, Huaipeng Gu, Liang-ming Yan, A. Cherepanov, V. Ovcharenko, V. Drozdov
{"title":"Modification of the structure and properties of heat-resistant alloys with the help of nanopowders of refractory compounds","authors":"C. La-mei, Guangxun Liu, Huaipeng Gu, Liang-ming Yan, A. Cherepanov, V. Ovcharenko, V. Drozdov","doi":"10.1109/3M-NANO.2012.6472998","DOIUrl":null,"url":null,"abstract":"Influence of nanodispersed refractory compounds on structure and mechanical properties of heat-resistant alloys K403 and K4169 was investigated. Powders of chemical compounds TiN, TiCN, Y2O3 and their mixtures were used as the modifying agents. The results show that the modifying leads to general improvement of grain and carbide structure of heat-resistant alloys in casts. The grain average size in the cast decreased by 2-3 times, the carbide grains size decreased from 40-60 μm to 10-20 μm. This leads to significant improvement of the life at breaking load and LCF properties of the cast.","PeriodicalId":134364,"journal":{"name":"2012 International Conference on Manipulation, Manufacturing and Measurement on the Nanoscale (3M-NANO)","volume":"305 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2012-08-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"3","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"2012 International Conference on Manipulation, Manufacturing and Measurement on the Nanoscale (3M-NANO)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/3M-NANO.2012.6472998","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 3
Abstract
Influence of nanodispersed refractory compounds on structure and mechanical properties of heat-resistant alloys K403 and K4169 was investigated. Powders of chemical compounds TiN, TiCN, Y2O3 and their mixtures were used as the modifying agents. The results show that the modifying leads to general improvement of grain and carbide structure of heat-resistant alloys in casts. The grain average size in the cast decreased by 2-3 times, the carbide grains size decreased from 40-60 μm to 10-20 μm. This leads to significant improvement of the life at breaking load and LCF properties of the cast.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们