Norhazeratul Mohammad Zainudin, Liew Pay Jun, Ching Yee Yap, Noraiham Mohamad, Jingsi Wang
{"title":"Effect of Peak Current and Pulse On Time on the Coating Layer Thickness using Electrical Discharge Coating","authors":"Norhazeratul Mohammad Zainudin, Liew Pay Jun, Ching Yee Yap, Noraiham Mohamad, Jingsi Wang","doi":"10.37934/mjcsm.6.1.1420","DOIUrl":null,"url":null,"abstract":"The present study focused on the surface modification of aluminum 6061 by using electrical discharge coating (EDC) with powder suspension. The effects of peak current (Ip) and pulse on time (Ton) on the coating layer thickness were investigated. This study used Tungsten powder as an additive and mixed it with the kerosene oil and surfactant Span 83. The results indicated that peak current and pulse on-time significantly affected the coating layer thickness. The thinnest coating layer was observed at 3A, 150 µs, while the thickest coating layer with an average value of 17.239 µm was obtained at parameter 4A and 250 µs. In conclusion, the high value of peak current and longer pulse duration on time increased the thickness of the coating layer.","PeriodicalId":419270,"journal":{"name":"Malaysian Journal on Composites Science and Manufacturing","volume":"35 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2021-11-15","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Malaysian Journal on Composites Science and Manufacturing","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.37934/mjcsm.6.1.1420","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
The present study focused on the surface modification of aluminum 6061 by using electrical discharge coating (EDC) with powder suspension. The effects of peak current (Ip) and pulse on time (Ton) on the coating layer thickness were investigated. This study used Tungsten powder as an additive and mixed it with the kerosene oil and surfactant Span 83. The results indicated that peak current and pulse on-time significantly affected the coating layer thickness. The thinnest coating layer was observed at 3A, 150 µs, while the thickest coating layer with an average value of 17.239 µm was obtained at parameter 4A and 250 µs. In conclusion, the high value of peak current and longer pulse duration on time increased the thickness of the coating layer.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们