Polyaniline based composite sorbents as carriers and delivery systems of biologically active substances Сорбенты на основе композитов полианилина в качестве носителей и систем доставки биологически активных соединений

Abstract

Sorption properties of polyaniline (PANI) have been investigated. It has been found that maximum amount of adsorbed glycerin by PANI reaches 78 wt.%, and material remaining as dry powder of black color. Nicotine (NCT) release in aerosol mixture with glycerin (GLY) from samples of PANI containing nicotine and 64-78 wt.% of glycerin was determined in test bench trial in 1l/min airstream at 2000C of heating. TG-MS and DSC analysis data showed that in the case of a sample with 64 wt.% % glycerin, less energy is required to desorb the glycerin + nicotine mixture than in the other two cases with bigger amount of glycerin. Hybrid PANI-SiO2 nanocomposites were synthesized and tested. In regard to glycerin sorption they are significantly inferior to PANI. Исследованы сорбционные свойства полианилина (ПАНИ). Установлено, что максимальное количество адсорбированного глицерина полианилином достигает 78 масс. %, а материал остается в виде сухого по- рошка черного цвета. Высвобождение никотина аэрозольной смесью глицерина из образцов ПАНИ, со- держащих никотин и 64-78 масс % глицерина определяли в испытаниях на стенде в потоке воздуха скоростью 1 л/мин при температуре 2000C. Данные ТГ-МС и ДСК анализа показали, что в случае образца с 64 масс. % глицерина для десорбции смеси глицерин + никотин требуется меньше энергии, чем в двух других случаях с большим количеством глицерина. Синтезированы и исследованы гибридные нанокомпозиты ПАНИ-SiO2. По сорбции глицерина они значительно уступают ПАНИ.