Using of mechanoactivation for preparation of cerium-containing solid solutions based on zircon

Abstract

Solid-phase synthesis of cerium-containing solid solutions based on ZrSiO4 was described. The synthesis was carried out using mechanical activation of a mixture consisting of zirconium oxide and hydrated amorphous silica with the addition of cerium oxide at a molar ratio of ZrО2:SiО2:CeО2 equal to 0.95:1.00:0.05. The mechanically activated in a centrifugal planetary mill mixture of reagents was calcined in the temperature range of 1200–1600 °C for 3 hours, which was accompanied by the essentially complete synthesis of zircon. The cerium content in the zircon structure was calculated from X-ray powder diffraction data.