Improving Fatigue Properties of 316L Stainless Steel Welded Joints by Surface Spinning Strengthening

IF 2.9 2区 材料科学 Q2 METALLURGY & METALLURGICAL ENGINEERING Acta Metallurgica Sinica-English Letters Pub Date : 2024-02-29 DOI:10.1007/s40195-024-01668-2
Dongqiqiong Wang, Qiang Wang, Xiaowu Li, Zhefeng Zhang
{"title":"Improving Fatigue Properties of 316L Stainless Steel Welded Joints by Surface Spinning Strengthening","authors":"Dongqiqiong Wang, Qiang Wang, Xiaowu Li, Zhefeng Zhang","doi":"10.1007/s40195-024-01668-2","DOIUrl":null,"url":null,"abstract":"<p>The surface spinning strengthening (3S) mechanism and fatigue life extension mechanism of 316L stainless steel welded joint were systematically elucidated by microstructural analyses and mechanical tests. Results indicate that surface gradient hardening layer of approximately 1 mm is formed in the base material through grain fragmentation and deformation twin strengthening, as well as in the welding zone composed of deformed <i>δ</i>-phases and nanotwins. The fatigue strength of welded joint after 3S significantly rises by 32% (from 190 to 250 MPa), which is attributed to the effective elimination of surface geometric defects, discrete refinement of <i>δ</i>-Fe phases and the appropriate improvement in the surface strength, collectively mitigating strain localization and surface fatigue damage within the gradient strengthening layer. The redistributed fine <i>δ</i>-Fe phases benefited by strong stress transfer of 3S reduce the risk of surface weak phase cracking, causing the fatigue fracture to transition from microstructure defects to crystal defects dominated by slip, further suppressing the initiation and early propagation of fatigue cracks.</p>","PeriodicalId":457,"journal":{"name":"Acta Metallurgica Sinica-English Letters","volume":null,"pages":null},"PeriodicalIF":2.9000,"publicationDate":"2024-02-29","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Acta Metallurgica Sinica-English Letters","FirstCategoryId":"1","ListUrlMain":"https://doi.org/10.1007/s40195-024-01668-2","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 0

Abstract

The surface spinning strengthening (3S) mechanism and fatigue life extension mechanism of 316L stainless steel welded joint were systematically elucidated by microstructural analyses and mechanical tests. Results indicate that surface gradient hardening layer of approximately 1 mm is formed in the base material through grain fragmentation and deformation twin strengthening, as well as in the welding zone composed of deformed δ-phases and nanotwins. The fatigue strength of welded joint after 3S significantly rises by 32% (from 190 to 250 MPa), which is attributed to the effective elimination of surface geometric defects, discrete refinement of δ-Fe phases and the appropriate improvement in the surface strength, collectively mitigating strain localization and surface fatigue damage within the gradient strengthening layer. The redistributed fine δ-Fe phases benefited by strong stress transfer of 3S reduce the risk of surface weak phase cracking, causing the fatigue fracture to transition from microstructure defects to crystal defects dominated by slip, further suppressing the initiation and early propagation of fatigue cracks.

Abstract Image

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
通过表面旋压强化提高 316L 不锈钢焊接接头的疲劳性能
通过微观结构分析和力学试验,系统地阐明了 316L 不锈钢焊接接头的表面旋转强化(3S)机理和疲劳寿命延长机理。结果表明,通过晶粒破碎和变形孪生强化,在母材中形成了约 1 mm 的表面梯度硬化层,在焊接区也形成了由变形 δ 相和纳米晶组成的表面梯度硬化层。3S 后焊接接头的疲劳强度显著提高了 32%(从 190 兆帕提高到 250 兆帕),这归功于表面几何缺陷的有效消除、δ-铁相的离散细化以及表面强度的适当提高,它们共同减轻了梯度强化层内的应变局部化和表面疲劳破坏。通过 3S 的强应力传递而重新分布的精细 δ-Fe 相降低了表面弱相开裂的风险,使疲劳断裂从微观结构缺陷过渡到以滑移为主的晶体缺陷,进一步抑制了疲劳裂纹的产生和早期扩展。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
Acta Metallurgica Sinica-English Letters
Acta Metallurgica Sinica-English Letters METALLURGY & METALLURGICAL ENGINEERING-
CiteScore
6.60
自引率
14.30%
发文量
122
审稿时长
2 months
期刊介绍: This international journal presents compact reports of significant, original and timely research reflecting progress in metallurgy, materials science and engineering, including materials physics, physical metallurgy, and process metallurgy.
期刊最新文献
Effects of Post-Heat Treatment and Carbide Precipitates on Strength-Ductility Balance of GH3536 Superalloy Prepared by Selective Laser Melting High Strength and Heat Resistance of Low-RE-Containing Mg Alloy Achieved via Substantial Dynamic Precipitates First-Principles Calculations on Electronic Structure, Adhesion Strength, and Interfacial Stability of Mg(0001)/AlB2(0001) Nucleation Interface Influence of Substituting W for Nb or Hf on Solidification Behavior of a Typical Co–Ni–Al–W Based Superalloy Effect of Ta on Tensile Behavior and Deformation Mechanism of a Nickel-Based Single Crystal Superalloy
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1